本发明专利技术公开了建筑材料领域内的一种混凝土防冻剂，由占重量百分比的以下成分组成：聚羧酸减水剂12~15%；二异丙醇胺12~18%；木质素磺酸钙6~8%；硝酸钙4~6%；聚乙二醇2~5%；对苯二甲酸3~7%；并用蒸馏水补足至100%，其中，所述含锰化合物的化学分子式为 C38H32N2O13Mn，本发明专利技术的混凝土防冻剂由有机、无机等多种材料配制而成，可显著提高混凝土的负温养护 7 天的强度。而且本发明专利技术的混凝土防冻剂和各类水泥均有较好的适应性，能够最大程度的发挥各种材料的性能。

A concrete antifreeze agent

The present invention discloses the field of building materials in a concrete antifreeze, which consists of the following components in weight percentage: polycarboxylate superplasticizer 12~15%; two isopropyl alcohol amine 12~18%; calcium lignosulfonate 6~8%; calcium 4~6%; polyethylene glycol 2~5%; terephthalic acid 3~7%; and with distilled water up to 100%, among them, chemical formula the manganese compound is C38H32N2O13Mn, concrete antifreeze of the present invention consists of various organic and inorganic materials, can significantly improve the negative temperature curing 7 days concrete strength. Moreover, the concrete antifreeze and various kinds of cement have good adaptability, and can maximize the performance of all kinds of materials.

【技术实现步骤摘要】
一种混凝土防冻剂
本专利技术涉及一种建筑材料助剂，特别涉及一种混凝土防冻剂。
技术介绍
在低温下为了保证工程的质量防止混凝土发生冻害，主要采取两种防护措施，一是采用覆盖或者围护升温方法防止混凝土温度降至0℃以下，此方法成本高、操作过程复杂；二是在混凝土中掺加防冻剂，该方法施工简单，效果也较好，因此在我国得到了广泛应用。
技术实现思路
本专利技术的目的是提供一种混凝土防冻剂，解决现有技术中的不足。本专利技术的目的是这样实现的：一种混凝土防冻剂，由占重量百分比的以下成分组成：聚羧酸减水剂12~15%；二异丙醇胺12~18%；木质素磺酸钙6~8%；硝酸钙4~6%；聚乙二醇2~5%；对苯二甲酸3~7%；并用蒸馏水补足至100%，其中，所述含锰化合物的化学分子式为C38H32N2O13Mn。与现有技术相比，本专利技术的有益效果在于：本专利技术的混凝土防冻剂由有机、无机等多种材料配制而成，可显著提高混凝土的负温养护7天的强度。而且本专利技术的混凝土防冻剂和各类水泥均有较好的适应性，能够最大程度的发挥各种材料的性能。具体实施方式实施例1一种混凝土防冻剂，由占重量百分比的以下成分组成：聚羧酸减水剂12%本文档来自技高网...

【技术保护点】
一种混凝土防冻剂，其特征在于，由占重量百分比的以下成分组成：聚羧酸减水剂 12~15% ；二异丙醇胺 12~18% ；木质素磺酸钙 6~8% ；硝酸钙 4~6% ；聚乙二醇 2~5% ；对苯二甲酸 3~7% ；并用蒸馏水补足至 100%，其中，所述含锰化合物的化学分子式为 C38H32N2O13Mn。

【技术特征摘要】
1.一种混凝土防冻剂，其特征在于，由占重量百分比的以下成分组成：聚羧酸减水剂12~15%；二异丙醇胺12~18%；木质素磺酸钙6~8%；硝...

【专利技术属性】
技术研发人员：张小勇，
申请(专利权)人：张小勇，
类型：发明
国别省市：江苏,32