一种粉煤灰中选铁的方法技术
A method of iron selection in fly ash
The invention discloses a method of iron selection in fly ash, which includes the following steps: (1) slurry (2) strong magnetic coarse selection (3) fine grinding (4) weak magnetic selection. According to the invention of iron rich beads in fly ash characteristics, by mixing magnetic roughing fine grinding process of magnetic weak selection, simple process, easy operation, convenient maintenance, and by fine grinding and two level mining, the iron ore recovery rate at the same time, great high grade iron ore concentrate grade recovery, to reach 55% to 65%, iron ore refining and fully meet the demand for cement additives.
【技术实现步骤摘要】
一种粉煤灰中选铁的方法
本专利技术属于固废资源利用和矿物加工
，具体涉及一种粉煤灰磁选铁的方法。
技术介绍
粉煤灰是一种混合物，它包含品种繁多的物质。精细利用是将他们一一分选出来，按各自的特性，将其中高附加值的品种充分利用，以达到物尽其用，提高粉煤灰综合利用的经济效益。粉煤灰按其颗粒分类可分为珠状颗粒和渣状颗粒两大类，在珠状颗粒中包括漂珠(也称空心微珠)、空心沉珠、复珠(子母珠)、密实沉珠(实心微珠)和富铁玻璃微珠等五大品种。其中富铁玻璃体除少量溶融于密实玻璃微珠中，绝大部分以显微状的磁铁矿和赤铁矿构成珠状颗粒，其粒径为10～150μm。各电厂粉煤灰中的富铁玻璃微珠含量不一，主要与原煤含铁量和燃烧工况等因素有关。根据经验，粉煤灰中含铁量在5％以上的，即有分选价值。从粉煤灰中分选提取富铁玻璃微珠具有较好的经济价值，而从现有选铁工艺可知，若采用强磁选铁，铁精矿的回收率较高，但质量品位却逐步下降；若采用弱磁选铁，铁精矿的质量品位较好，但回收率较低。
技术实现思路
本专利技术目的是：提供一种新的选铁工艺方法，即强磁粗选+细磨+弱磁精选的工艺方法。该工艺方法选铁不仅回收率...
【技术保护点】
一种粉煤灰中选铁的方法，其特征在于：包括以下步骤：(1)调浆：将粉煤灰输送进入调浆池，然后加水调质，将水和粉煤灰的质量比调整至4：1～9：1，搅拌均匀，此时粉煤灰灰浆含水率为80～90％，含固率为10～20％；(2)强磁粗选：将调浆后物料输送进入强磁磁选机，磁场强度5000～7000Gs，经强磁粗选后，铁矿提取量的质量百分比为10％～15％，铁品位提高到45％～50％；(3)细磨：将粗选后的铁矿浆输送至湿式球磨机，经细磨后，粗铁矿粒径达到0.07‑0.074mm；(4)弱磁精选：将经粗选、细磨后铁矿浆输送至弱磁磁选机，磁场强度800～1000Gs，经弱磁精选后，铁矿提取量的...
【技术特征摘要】
1.一种粉煤灰中选铁的方法，其特征在于：包括以下步骤：(1)调浆：将粉煤灰输送进入调浆池，然后加水调质，将水和粉煤灰的质量比调整至4：1～9：1，搅拌均匀，此时粉煤灰灰浆含水率为80～90％，含固率为10～20％；(2)强磁粗选：将调浆后物料输送进入强磁磁选机，磁场强度5000～7000Gs，经强磁粗选后，铁矿提取量的质量百分比为10％～15％，铁品位提高到45％～50％；(3)细磨：将粗选后的铁矿浆输送至湿式球磨机，经细磨后，粗铁矿粒径达到0.07-0.074mm；(4)弱磁精选：将经粗选、细磨后铁矿浆输送至弱磁磁选机，磁场强度800～1000Gs，经弱磁精选后，铁矿提取量的质量百分比为5％～12％，铁品位提高到55％～65％。2.根据权利要求1所述的一种粉煤灰中选铁的方法，其特征在于...
【专利技术属性】
技术研发人员：金涛，李刚，陈科宇，黄泽林，
申请(专利权)人：四川深蓝环保科技有限公司，
类型：发明
国别省市：四川,51