Disclosed is a glass, its composition comprises the following oxides (wt%):SiO2 70%, Al2O3 61 0 9%, Na2O 13%, K2O 10 0 1%, MgO 6%, CaO 2 6 16%, SrO 1%, ZrO2 0 2 15% TiO2, 0 1%. The glass may have a strain of more than 570 DEG C, and has good dimensional stability at high temperature, making them suitable for processing at elevated temperatures and fireproof glass substrate, such as substrate for display panel, information storage disc and a semiconductor device includes a photovoltaic cell. The physical properties of glass are disclosed, such as thermal expansion coefficient, density and index of refraction, and melting and liquidus temperature. The glass is suitable for manufacturing by floatation, and plate glass is produced in sheet form.
【技术实现步骤摘要】
【国外来华专利技术】新玻璃本专利技术涉及玻璃，更具体地涉及新玻璃、新玻璃组合物和由新玻璃组合物构成的基材。新玻璃组合物是钠钙硅玻璃，但与已知的钠钙硅玻璃，特别是通常用于通过浮法工艺生产平板玻璃的那些钠钙硅玻璃相比，具有相对高的应变点。因此，本专利技术的新玻璃适用于在高温下需要良好尺寸稳定性的应用，例如防火窗玻璃和用于在高温下加工的基材。这些基材适用于涂层的沉积和显示面板、盘例如磁记录盘、半导体器件包括光伏电池，特别是太阳能电池的制造等应用。虽然普通钠钙硅玻璃(即常用于建筑物和车辆的窗户和其他窗玻璃的钠钙硅玻璃组合物)对于许多上述应用具有在室温下的合适性能，但是这些应用可能需要在高温下加工玻璃，即在高于应变点，或退火点，或甚至玻璃的软化点的温度下。在这样升高的温度下加工玻璃会导致在玻璃中产生永久的内部应力，可能导致玻璃的变形或断裂。在加工过程中，玻璃甚至可变得畸变或变形。因此，已经尝试提供更适合于高温加工的玻璃，即由于具有相对高的应变点而具有改善的高温稳定性的玻璃。通常使用的钠钙浮法玻璃的应变点(其定义为玻璃的粘度为1014.5泊的温度，表示为Tlog14.5泊)在约510℃至540℃的...
【技术保护点】
玻璃，具有包含以下氧化物的组成(以重量％计)：
【技术特征摘要】
【国外来华专利技术】2015.03.26 GB 1505096.61.玻璃，具有包含以下氧化物的组成(以重量％计)：2.根据权利要求1所述的玻璃，其包含以下氧化物(以重量％计)：3.根据权利要求1或2所述的玻璃，其包含3-12％的ZrO2，优选3至11％的ZrO2，更优选4至10％的ZrO2，更优选6至10％的ZrO2。4.根据前述权利要求中任一项所述的玻璃，其具有大于570℃，优选大于580℃，更优选大于590℃的应变点。5.根据前述权利要求中任一项所述的玻璃，其具有小于1500℃，优选小于1480℃，更优选小于1460℃的熔化温度(在该温度下粘度＝log2泊)。6.根据前述权利要求中任一项所述的玻璃，其具有小于1200℃，优选小于1180℃，更优选小于1160℃，更优选小于1140℃，更优选小于1120℃，最优选小于1100℃的液相线温度。7.根据前述权利要求中任一项...
【专利技术属性】
技术研发人员：M·J·豪斯勒，S·泰勒，
申请(专利权)人：皮尔金顿集团有限公司，
类型：发明
国别省市：英国,GB
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。