The invention discloses a permeable pavement paving for environmental protection color binder, which is composed of the following raw materials quality percentage: 50 to 64% aromatic oil, 32 ~ 40% C9 petroleum resin, 1 ~ 2%, 3 ~ 8% chlorinated polyethylene rubber adjacent benzene two formic acid two octanoic acid, 0 ~ 1% modified three Triallyl isocyanurate. The invention also discloses the preparation method of the environmental protection color cementing material for the paving of the permeable pavement. The environmental friendly color cementing material prepared by the method of the invention has high and low temperature performance, good adhesion, strong water resistance and durability.
【技术实现步骤摘要】
透水型路面铺筑用环保彩色胶结料及其制备方法
本专利技术属于道路材料领域，具体涉及一种透水型路面铺筑用环保彩色胶结料及其制备方法。
技术介绍
彩色沥青路面是将浅色沥青胶结料、集料、无机颜料等在拌合后经过摊铺、碾压而成，该类型路面具有丰富的色彩选择、优良的理化性能、亲善的环境协调功能，因而越来越受到青睐与重视，在公园、自行车道、公交汽车专线和景观道路等方面得到了广泛应用。应用于城市道路时的优点是：可以提高路面美观；使道路功能分区，便于诱导交通；提高驾驶员的警觉性和识别效果，增强道路通行能力和行车安全。透水型路面是一种开级配、大空隙率的路面，其空隙率一般在15～25％左右，能够及时将路面积水渗入至其下方的不透水层后通过路肩处排水系统，实现路面积水的快速排出，从而减轻道路积水对路面结构的损害。此外，开级配、大空隙率的路面还能够增强道路的抗滑性能，同时也可以吸收车辆运行时所产生的噪音，显著降低城市交通噪音，提高车辆驾驶者及周边居民的舒适性。因此，将彩色胶结料应用于铺筑透水型路面，则新建成的彩色透水型路面将同时具有彩色沥青路面和透水型路面的优点。同时，这也对彩色胶结料的性能提...
【技术保护点】
透水型路面铺筑用环保彩色胶结料，其特征在于，由以下质量百分比的原料组成：50～64％的芳烃油、32～40％的C9石油树脂、1～2％的氯化聚乙烯橡胶、3～8％的邻苯二甲酸二辛酸、0～1％的改性三烯丙基异氰脲酸酯。
【技术特征摘要】
1.透水型路面铺筑用环保彩色胶结料，其特征在于，由以下质量百分比的原料组成：50～64％的芳烃油、32～40％的C9石油树脂、1～2％的氯化聚乙烯橡胶、3～8％的邻苯二甲酸二辛酸、0～1％的改性三烯丙基异氰脲酸酯。2.根据权利要求1所述的透水型路面铺筑用环保彩色胶结料，其特征在于：所述改性三烯丙基异氰脲酸酯由三烯丙基异氰脲酸酯与SiO2按照70％：30％的质量比混合而得。3.根据权利要求2所述的透水型路面铺筑用环保彩色胶结料，其特征在于：由以下质量百分比的原料组成：56.4％的芳烃油，38.5％的C9石油树脂、1.4％的氯化聚乙烯橡胶、3.2％的邻苯二甲酸二辛酸和0.5％的改性三烯丙基异氰脲酸酯。4.如权利要求1～3任一所述的透水型路面铺筑用环保彩色胶结料的制备方法，其特征在于包括...
【专利技术属性】
技术研发人员：王修山，凡涛涛，常晟，
申请(专利权)人：浙江理工大学，
类型：发明
国别省市：浙江,33