本发明专利技术涉及PVC扣板的技术领域，特别涉及一种功能性PVC扣板。所述PVC扣板由下述重量配比的各组分组成，PVC 80～85份，轻质碳酸钙20～25份，改性剂5～8份，石蜡1～3份，荧光剂3～5份，石英石粉1～3份，苯丙三氮唑1～2份，硫酸锶1～3份，硝酸银1～3份，钛白粉2～4。本发明专利技术与现有技术相比的有益效果是：本发明专利技术的扣板材质重量轻、安装简便，抗压力性强，耐候性好，同时还具有夜光功能，便于夜间方便出入厨房或卫生间。

A functional PVC buckle

The invention relates to the technical field of PVC buckle plate, in particular to a functional PVC buckle. The PVC plate by the group to the weight of components, PVC from 80 to 85, 20 to 25 portions of light calcium carbonate, modifier of 5 to 8, 1 to 3 portions of paraffin, fluorescent agent 3 ~ 5, 1 ~ 3 quartz powder, Ben Bingsan triazole 1 ~ 2 copies. Strontium sulfate 1 ~ 3, 1 ~ 3 of silver nitrate, titanium dioxide, 2 ~ 4. Compared with the prior art, the invention has the beneficial effects that the buckle plate has the advantages of light weight, simple installation, strong pressure resistance, good weather resistance, and night luminous function, and is convenient for entering the kitchen or toilet at night.

【技术实现步骤摘要】
一种功能性PVC扣板
本专利技术涉及PVC扣板的
，特别涉及一种功能性PVC扣板。
技术介绍
PVC扣板是以聚氯乙烯树脂为基料，加入一定量抗老化剂，改性剂等助剂，经混炼、压延、真空吸塑等工艺而制成的。这种PVC扣板吊顶特别适用于厨房、卫生间的吊顶装饰，具有质量轻、防潮湿、隔热保温、不易燃烧、不吸尘、易清洁、可涂饰、易安装、价格低等优点。但抗压力性差，而且功能单一。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种功能性PVC扣板。为实现上述目的，本专利技术采用的技术方案是：本专利技术所述的一种功能性PVC扣板，所述PVC扣板由下述重量配比的各组分组成，PVC80～85份，轻质碳酸钙20～25份，改性剂5～8份，石蜡1～3份，荧光剂3～5份，石英石粉1～3份，苯丙三氮唑1～2份，硫酸锶1～3份，硝酸银1～3份，钛白粉2～4。进一步地，所述PVC扣板由下述重量配比的各组分组成，PVC80份，轻质碳酸钙25份，改性剂8份，石蜡3份，荧光剂5份，石英石粉3份，苯丙三氮唑2份，硫酸锶3份，硝酸银3份，钛白粉4份。本专利技术与现有技术相比的有益效果是：本专利技术的扣板材质重本文档来自技高网...

【技术保护点】
一种功能性PVC扣板，其特征在于：所述PVC扣板由下述重量配比的各组分组成，PVC 80～85份，轻质碳酸钙 20～25份，改性剂 5～8份，石蜡1～3份，荧光剂3～5份，石英石粉1～3份，苯丙三氮唑 1～2份，硫酸锶1～3份，硝酸银1～3份，钛白粉2～4。

【技术特征摘要】
1.一种功能性PVC扣板，其特征在于：所述PVC扣板由下述重量配比的各组分组成，PVC80～85份，轻质碳酸钙20～25份，改性剂5～8份，石蜡1～3份，荧光剂3～5份，石英石粉1～3份，苯丙三氮唑1～2份，硫酸锶1～3份，硝酸银1～3份，钛...

【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：黄宇松，
类型：发明
国别省市：广东,44