The invention discloses a technology in the field of food packaging a food packaging bag and preparation method thereof, the food packaging bag comprises the following raw materials in parts by weight: 20 to 25 portions of polyvinyl alcohol and starch from 70 to 80, 7 to 11 portions of straw fiber and antioxidants from 2 to 4, 2 to 3 portions of plasticizer and the degradation promoter 1 - 1.5, 2 - 4, Zinc Oxide filler 2 ~ 4 whisker. And the method for preparing the food packaging bags, packaging bags and its degradation rate faster, buried 100 days later, it can degrade 40% of the weight, the effect is very obvious, and with no pollution for the environment material degradation, will not cause pollution to the environment, often in environmental protection.
【技术实现步骤摘要】
一种食品包装袋及其制备方法
本专利技术属于食品包装
，具体涉及一种食品包装袋及其制备方法。
技术介绍
目前常用的聚乙烯(PE)和聚丙烯(PP)塑料包装袋由于质量轻、价格低廉、使用便捷等优点被广泛应用于人们的日常生活中。但是它在丰富和方便人民生活的同时，由于其主要成分在自然环境中难以分解，因而造成了严重的“白色污染”问题。随着社会的可持续发展，生态环境问题已经被各国政府提高到了发展战略的高度，而研究和开发可完全生物降解塑料是解决塑料包装袋废弃物带来的“白色污染”问题的重要途径。聚乙烯醇(PVA)因具有多羟基、强氢键等特点，被赋予很多优异的性能；同时它还可通过非石油化工路线合成的，故而在石油资源日益枯竭的背景下，这种材料更具有重要的应用价值。根据专家预测，未来几年全球PVA薄膜产量的年平均增长率将达到8～10％。与其它薄膜相比，PVA薄膜不仅具有高透明性、耐油性、气体高隔阻性和不同程度的水溶性，更为重要的是，PVA在湿环境中有细菌存在的条件下6个月内可以完全分解成水和CO2，是完全生物降解材料。但是PVA的降解对降解环境要求较高，使降解速度还是显得相对较慢，且无...
【技术保护点】
一种食品包装袋，其特征在于：由以下重量份数的原料组成：聚乙烯醇20～25份、淀粉70～80份、秸秆纤维7～11份、抗氧剂2～4份、增塑剂2～3份、降解促进剂1～1.5份、填充剂2～4份、氧化锌晶须2～4份。
【技术特征摘要】
1.一种食品包装袋，其特征在于：由以下重量份数的原料组成：聚乙烯醇20～25份、淀粉70～80份、秸秆纤维7～11份、抗氧剂2～4份、增塑剂2～3份、降解促进剂1～1.5份、填充剂2～4份、氧化锌晶须2～4份。2.如权利要求1所述的食品包装袋，其特征在于：由以下重量份数的原料组成：聚乙烯醇23份、淀粉73份、秸秆纤维8份、抗氧剂3份、增塑剂3份、降解促进剂1份、填充剂3份、氧化锌晶须3份。3.如权利要求1所述的食品包装袋，其特征在于：所述淀粉为玉米淀粉和土豆淀粉的混合物，玉米淀粉和土豆淀粉的重量比为1:1。4.如权利要求1所述的食品包装袋，其特征在于：所述抗氧剂为2，6-三级丁基-4-甲基苯酚。5.如权利要求1所述的食品包装袋，其特征在于：所述增塑剂为甘油。6.如权利要求1所述...
【专利技术属性】
技术研发人员：张建平，
申请(专利权)人：广德美好包装科技有限公司，
类型：发明
国别省市：安徽,34