层状氯氧化铋可见光催化剂的制备方法及其应用技术
Preparation and application of visible light catalyst for bismuth oxide layer
The invention discloses a preparation method and application of a layered bismuth oxide visible light catalyst. The preparation method comprises bismuth nitrate and polyvinylpyrrolidone dissolved in ethylene glycol, A; ammonium chloride and sodium hydroxide dissolved in water, B phase; then the combination of A and B, the mixture of hydrothermal reaction, reaction, filtering, washing and drying, get layered chloride bismuth oxide visible light catalyst, molecular formula of bismuth oxychloride is Bi12O17Cl2. The catalyst prepared by the method has the advantages of good controllability, easy to mass synthesis and so on, and can be used to efficiently degrade the wastewater of organic pollutants.
【技术实现步骤摘要】
层状氯氧化铋可见光催化剂的制备方法及其应用
本专利技术属于可见光催化领域，涉及一种层状氯氧化铋可见光催化剂的制备方法及其应用，具体涉及一种层状氯氧化铋可见光催化剂的制备方法及其在可见光下催化降解废水中的有机污染物的应用。
技术介绍
目前，随着化石能源短缺，太阳能转化成化学能逐渐引起了研究者的兴趣。半导体光催化技术是通过光催化剂在光照射下产生的催化反应，是可以模拟大自然中的光合作用的一种技术。光通过在光催化剂的表面进行激发可以产生空穴和电子，空穴与电子可以与水进行自由基传递，产生氧气、氢气，同时也会产生羟基自由基或者超氧自由基使有机污染物进行降解，从而实现光能的转化。光催化氧化作为一种高级氧化技术，具有氧化能力强、无二次污染等优点，从而成为处理废水的新途径。然而，目前的半导体光催化剂由于带隙较宽，如TiO2、ZnO、BiOCl和SnO2只能吸收紫外光进行反应。由于紫外光在太阳光中的比例较小，使得光催化剂不能很好的利用太阳光，所以开发可见光响应的光催化剂显得十分有必要。作为一类重要的光催化剂，BiOCl的带隙较宽，一直得不到很好的重视。虽然DFT计算揭示了调整Bi、O...
【技术保护点】
一种层状氯氧化铋可见光催化剂的制备方法，其特征在于，包括以下步骤：将硝酸铋与聚乙烯吡咯烷酮溶于乙二醇中，得到A相；将氯化铵和氢氧化钠溶于水中，得到B相；再将A相和B相混合，所得混合液进行水热反应，反应后，经过滤、洗涤和烘干，得到层状氯氧化铋可见光催化剂，氯氧化铋的分子式为Bi12O17Cl2。
【技术特征摘要】
1.一种层状氯氧化铋可见光催化剂的制备方法，其特征在于，包括以下步骤：将硝酸铋与聚乙烯吡咯烷酮溶于乙二醇中，得到A相；将氯化铵和氢氧化钠溶于水中，得到B相；再将A相和B相混合，所得混合液进行水热反应，反应后，经过滤、洗涤和烘干，得到层状氯氧化铋可见光催化剂，氯氧化铋的分子式为Bi12O17Cl2。2.根据权利要求1所述的层状氯氧化铋可见光催化剂的制备方法，其特征在于，所述硝酸铋与聚乙烯吡咯烷酮的质量比为100∶1～2，所述硝酸铋与乙二醇的质量体积比为2g∶20mL～30mL。3.根据权利要求1所述的层状氯氧化铋可见光催化剂的制备方法，其特征在于，所述氯化铵与氢氧化钠的质量比为1∶3～4，所述氢氧化...
【专利技术属性】
技术研发人员：曾光明，周成赟，黄丹莲，赖萃，张辰，程敏，胡亮，熊炜平，晏铭，李志豪，颜学磊，
申请(专利权)人：湖南大学，
类型：发明
国别省市：湖南,43