一种基台的表面改性方法技术
A surface modification method for base platform
The invention relates to a surface of the base station modification method comprises the following steps: alkali processing base; aqueous solution after alkali treatment base on 3 aminopropyltrimethoxysilane in ultrasonic reaction time; soaking water solution with ultrasonic reaction after abutment in graphene oxide in a for some time, and then transferred to dry naturally, minocycline hydrochloride by soaking in a period of time. The modified layer of graphene oxide loaded with minocycline is obtained on the surface of the abutment. It can improve the antibacterial property of the surface of the abutment and improve the cell compatibility of the base surface by using the contact sterilization of graphene oxide and the release and sterilization of minocycline hydrochloride.
【技术实现步骤摘要】
一种基台的表面改性方法
本专利技术属于金属材料表面改性
，具体涉及一种基台的表面改性方法。
技术介绍
随着口腔种植技术的不断发展，种植修复已渐渐成为患者缺牙的首选治疗方案，缺牙修复中种植修复能最大限度地恢复患者的咀嚼功能并且几乎没有异物感，已经越来越多的被人们所接受和认可。随着种植体的广泛运用，种植体周围炎也越来越多见。种植体周围炎是由细菌引起的破坏种植体周围支持组织的炎症。医用牙科种植体主要包括种植体、基台和牙冠三部分，其中基台直接与牙龈接触，最容易引发种植体周围炎的产生。为此，通过合适的表面改性技术，提高基台表面的抗菌性能已引起了广大牙科医学人员的关注。近年来，石墨烯以及衍生物，由于其优异的物理、化学及其生物学性能，在生物医学领域引起了广泛的关注。据报道，石墨烯及其衍生物具有良好的生物相容性，能够促进细胞的粘附、增殖，诱导骨髓间充质干细胞的成骨分化(ACSnano2011,5,4670-4678)，而且，石墨烯及其衍生物还表现出了优异的抗菌性能(J.Am.Chem.Soc.2016,128,6331-6339)。我们知道单层石墨烯只有0.34nm的厚度，...
【技术保护点】
一种基台的表面改性方法，其特征在于，包括以下步骤：基台的碱处理；碱处理后的基台置于3‑氨丙基三甲氧基硅烷的水溶液中超声反应一段时间；超声反应后的基台置于氧化石墨烯的水溶液中浸泡一段时间，然后自然晾干，转移到盐酸米诺环素的水溶液浸泡一段时间。
【技术特征摘要】
1.一种基台的表面改性方法，其特征在于，包括以下步骤：基台的碱处理；碱处理后的基台置于3-氨丙基三甲氧基硅烷的水溶液中超声反应一段时间；超声反应后的基台置于氧化石墨烯的水溶液中浸泡一段时间，然后自然晾干，转移到盐酸米诺环素的水溶液浸泡一段时间。2.根据权利要求1所述的方法，其特征在于，所述碱处理为将所述基台置于1～5mol/L的氢氧化钠溶液中，置于摇床摇晃6～12小时，摇床转速为50～100rpm。3.根据权利要求2所述的方法，其特征在于，所述碱处理为将所述基台置于5mol/L的氢氧化钠溶液中，置于摇床摇晃12小时，摇床转速为100rpm。4.根据权利要求1所述的方法，其特征在于，所述3-氨丙基三甲氧基硅烷的水溶液的体积比浓度为1～10％，所述超声反应的时间为2～4小时。5.根据权利要求4所述的方法，其特征在于，所述3-氨...
【专利技术属性】
技术研发人员：钱文昊，邱家军，刘宣勇，苏俭生，
申请(专利权)人：上海市徐汇区牙病防治所，
类型：发明
国别省市：上海,31