The invention discloses a high brightness silver foil with a mosaic decoration, consists of the following raw materials in weight portion: 40 silver 60 copies, 160 copies of the 150 powder, titanium powder 15 chromium powder 10 25 copies, 20 copies, 12 copies of the 6 nano silica. The invention of the mosaic decorated with silver foil with high brightness aluminum as the main raw material and adding silver and other raw materials, the price is cheaper Sterling silver. The silver foil with good ductility, easy processing and the finished product is thinner, cost savings. The invention of the silver foil all day more white light and high surface gloss, for better mosaic decorative effect.
【技术实现步骤摘要】
一种马赛克装饰用高亮度银箔
本专利技术涉及一种银箔，更确切地说，是一种马赛克装饰用高亮度银箔。
技术介绍
银箔用途较为广泛，适用于任何高档装饰的地方，如：寺院庙宇、佛像、宾馆酒店、豪宅、会所、仿古园林建筑、雕塑、家具、牌匾楹联等。也可以用于画、书、邮票、墙纸、装饰面板、瓷砖、马赛克、餐具、茶具、果盘、花瓶、玻璃盘、工艺品、招牌等的制作。银箔马赛克是一种将银箔贴附于马赛克原胚表面制成的装饰材料，马赛克贴在墙体表面银箔面一般位于马赛克的内面，银箔的光泽度会被马赛克的原胚遮盖一部分，这样银箔马赛克看起来整体较暗，装饰效果不佳。
技术实现思路
本专利技术主要是解决现有技术所存在的技术问题，从而提供一种马赛克装饰用高亮度银箔。本专利技术的上述技术问题主要是通过下述技术方案得以解决的：一种马赛克装饰用高亮度银箔，由如下重量份的原料组成：银粉40-60份，铝粉150-160份，钛粉15-25份，铬粉10-20份，纳米二氧化硅6-12份。所述马赛克装饰用高亮度银箔的制备方法：首先，将银粉、铝粉在坩埚中高温熔化成熔液，充分搅拌并保温30-40分钟，继续添加钛粉、铬粉和纳米二氧化硅，熔化...
【技术保护点】
一种马赛克装饰用高亮度银箔，其特征在于，由如下重量份的原料组成：银粉40‑60份，铝粉150‑160份，钛粉15‑25份，铬粉10‑20份，纳米二氧化硅6‑12份；所述马赛克装饰用高亮度银箔的制备方法：首先，将银粉、铝粉在坩埚中高温熔化成熔液，充分搅拌并保温30‑40分钟，继续添加钛粉、铬粉和纳米二氧化硅，熔化并充分搅拌10‑15分钟；然后，将所得熔液倒入度量铁槽内冷却，制成银条；最后，使用常规方法将所得银条制成银箔。
【技术特征摘要】
1.一种马赛克装饰用高亮度银箔，其特征在于，由如下重量份的原料组成：银粉40-60份，铝粉150-160份，钛粉15-25份，铬粉10-20份，纳米二氧化硅6-12份；所述马赛克装饰用高亮度银箔的制备方法：首先，将银粉、铝粉在坩埚中高温熔化成熔液，充分搅拌并保温30-40分钟，继续添加钛粉、铬粉和纳米二氧化硅，熔化并充分搅拌10-15分钟；...