The invention discloses an antifreeze liquid and a preparation method thereof, and relates to the technical field of antifreeze, includes the following components: alcohol from 30 to 80, the inhibitor 0.5 ~ 2, 0.1 ~ 0.5 pH buffer, defoaming agent 0.001 ~ 0.05, 0.2 ~ 0.8 mildewcide, dyeing agent 0.005 ~ 0.01 a deionized water from 15 to 60, according to the proportion of weighing alcohol and deionized water, stirring after sequentially adding corrosion inhibitor, defoaming agent, anti mildew agent, dyeing agent and pH buffering agent, after mixing the components, namely the antifreeze. The corrosion inhibitor of the invention is inorganic salt and organic carboxylic acid, and does not contain toxic substances such as molybdate, nitro aromatic substances, amine and nitrite. It is safe and environmental friendly, and has good corrosion inhibition effect on aluminum components, copper parts and steel components.
【技术实现步骤摘要】
一种防冻液及其制备方法
本专利技术涉及防冻液领域，更具体的是涉及一种对多种金属具有缓蚀作用的防冻液及其制备方法。
技术介绍
随着生活水平的提高，汽车已成为大部分人的代步工具，汽车护理也被越来越多的人所重视。其中，防冻液是车辆必备的一种保养品，它具有冬天防冻、夏天防沸的功能，能保护发动机的冷却系统，改善散热效果，提高发动机效率，是事关汽车“心脏”健康的保养品。防冻液接触的部件多为钢、铸铁、铝、黄铜等金属组成，它们在电解质作用下极易发生电化学腐蚀，同时防冻液中的二元醇类物质分解后会形成酸性产物，燃料燃烧后形成的酸性废气也会渗透到冷却系统中促进腐蚀的发生，因此防冻液中缓蚀剂的选择至关重要。目前常用的无机缓蚀剂如硅酸盐、磷酸盐、硼酸盐等，可防止铝部件的腐蚀，但易消耗，磷酸盐、硼酸盐对高温下的铸铝表面的缓蚀保护非常不利，现已受到严格限制，有机缓蚀剂如苯甲酸、三乙醇胺、苯并三氮唑等可防止铜质部件的腐蚀，但价格昂贵，因此为了保护汽车“心脏”，研制一种对多种金属具有缓蚀作用且环保的防冻液具有重要意义。
技术实现思路
本专利技术的目的在于：为了解决现有的防冻液对冷却系统各部件的腐蚀，防...
【技术保护点】
一种防冻液，其特征在于，该防冻液包括以下组分及重量份：醇类30～80份，复配缓蚀剂0.5～2份，pH缓冲剂0.1～0.5份，消泡剂0.001～0.05份，防霉剂0.2～0.8份，染色剂0.005～0.01份，去离子水15～70份。
【技术特征摘要】
1.一种防冻液，其特征在于，该防冻液包括以下组分及重量份：醇类30～80份，复配缓蚀剂0.5～2份，pH缓冲剂0.1～0.5份，消泡剂0.001～0.05份，防霉剂0.2～0.8份，染色剂0.005～0.01份，去离子水15～70份。2.根据权利要求1所述的一种防冻液，其特征在于，所述的醇类包括乙二醇和甘油，两者的重量份比为6:0～6:1。3.根据权利要求1所述的一种防冻液，其特征在于，所述的复配缓蚀剂为无机盐和有机羧酸复配，两者的重量份比为1:1～1:6。4.根据权利要求3所述的一种防冻液，其特征在于，所述的无机盐为硅酸盐、硝酸盐中的至少一种。5.根据权利要求3所述的一种防冻液，其特征在于，所述的有机羧酸为丁二酸、乙二酸、苯甲酸、癸酸、辛酸...
【专利技术属性】
技术研发人员：赵红昌，严芳芳，
申请(专利权)人：四川弘毅智慧知识产权运营有限公司，
类型：发明
国别省市：四川,51