The invention discloses a method used for furniture and decorative components with special-shaped coated moisture curable polyurethane hot melt adhesive, which comprises amorphous polyester polyol, polyester polyol, liquid crystalline polyester polyol and isocyanate component; the moisture curable polyurethane hot melt adhesive without organic solvent, solid content, viscosity and the beginning of 100% the final viscosity of high strength, good fluidity, positioning ability, bonding density, can reflect precisely the original beauty of art, can be widely used for medium and high density board, laminates, wood and other iron and steel, alloy and composite material (elliptic) circular surface and step surface, special-shaped surface encapsulation paste decoration.
【技术实现步骤摘要】
一种用于家具及装饰构件异形面包覆的湿固化聚氨酯热熔胶
本专利技术涉及一种包覆胶，特别涉及一种用于家具及装饰构件异形面包覆的湿固化聚氨酯热熔胶，属于胶粘剂
技术介绍
在建筑、家装领域中，经常要对一些家具及装饰构件非平整(异形)面部位进行涂贴包覆装饰，如木板、铝合金、不锈钢及木塑板等材料的端面。通过包覆装饰一方面可以阻止环境中的水分、酸、碱、微生物和害虫等对材料的侵蚀外，同时可以使家具或装饰构建更加美观。一般贴饰过程都要用到包覆胶，采用与包覆异形面相吻合的施胶和推压装置进行循序压合，在贴饰方面最重要的要求是保障基材与饰面膜之间快速固化，粘接密实、牢固，细致表现这些曲面的艺术美感。现有技术中包覆胶产品绝大部分都是以聚氨酯预聚体作为有效成分，采用有机溶剂，有机溶剂在生产和使用过程中会缓慢挥发，均破坏环境和危害操作人员健康。如中国专利(CN102838951A)公开了一种金属包覆胶粘剂及其制备方法，具体公开其主要原材料组成为丙烯酸酯类单体和溶剂，该方法采用了大量的酯类和甲苯有机溶剂，不但成本高，对环境造成污染。近年来，湿固化聚氨酯热熔胶粘剂(简称PUR)因其环保性...
【技术保护点】
一种用于家具及装饰构件异形面包覆的湿固化聚氨酯热熔胶，其特征在于：包括以下质量份组分：无定型聚酯多元醇20～50份；液体聚酯多元醇20～40份；结晶型聚酯多元醇30～50份；异氰酸酯10～20份。
【技术特征摘要】
2017.09.08 CN 20171080643591.一种用于家具及装饰构件异形面包覆的湿固化聚氨酯热熔胶，其特征在于：包括以下质量份组分：无定型聚酯多元醇20～50份；液体聚酯多元醇20～40份；结晶型聚酯多元醇30～50份；异氰酸酯10～20份。2.根据权利要求1所述的用于家具及装饰构件异形面包覆的湿固化聚氨酯热熔胶，其特征在于：所述无定型聚酯多元醇的分子量为1000～6000，Tg＝26～56℃。3.根据权利要求2所述的用于家具及装饰构件异形面包覆的湿固化聚氨酯热熔胶，其特征在于：所述无定型聚酯多元醇包括PN-110、dynacoll-7150、dynacoll-7130中至少一种。4.根据权利要求1～3任一项所述的用于家具及装饰构件异形面包覆的湿固化聚氨酯热熔胶，其特征在于：所述液体聚酯多元醇分子量为500～8000，Tg＝-30～-50℃。5.根据权利要求4所述的用于家具及装饰构件异形面包覆的湿固化聚氨酯热熔胶，其特征在于：所述液体聚酯多元醇包括dynacoll-7250和/或dyna...
【专利技术属性】
技术研发人员：舒跃辉，张耀根，
申请(专利权)人：广州市极威新材料有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。