负载型催化燃烧催化剂及制备和应用制造技术

本发明专利技术公开了一种负载型催化燃烧催化剂及制备和应用，该催化剂由载体和负载于载体上的活性组分组成；所述活性组分由氧化铜、三氧化钼和铜钼混合氧化物组成；其中活性组分中Cu与Mo摩尔比为1:0.5‑1:4；所述活性组分负载质量占载体质量的5％‑20％。浸渍法制备得到。本发明专利技术所使用的活性组分元素均为过渡金属和稀土金属氧化物，不含贵金属，成本低，并且具有高活性、高稳定性等优点。

Supported catalytic combustion catalyst and its preparation and Application

The present invention discloses a catalyst and preparation and application of a load type catalytic combustion, active component of the catalyst consists of a carrier and load on the carrier component; the active component is composed of copper oxide, molybdenum oxide and copper molybdenum mixed oxides; the active component in Cu and Mo molar ratio of 1:0.5 1:4; the active component of load quality accounted for 5% 20% carrier quality. The impregnation method is prepared. The active component elements used in the invention are transition metals and rare earth metal oxides, which do not contain noble metals, and have low cost and high activity and high stability.

【技术实现步骤摘要】
负载型催化燃烧催化剂及制备和应用
本专利技术涉及一种负载型催化燃烧催化剂及制备和应用，特别涉及一种用于催化燃烧挥发性有机废气苯乙烯的Cu-Mo/不同载体催化剂的制备方法，及其在催化燃烧苯乙烯有机废气中的应用。
技术介绍
挥发性有机化合物(VOCs)是指在常温下饱和蒸气压大于70Pa，常压下沸点在260℃以内的有机化合物。从环境监测角度来讲，指以氢焰离子检测器测出的非甲烷烃类检出物的总称，包括烃类、含卤烃类及硫烃类化合物。它是机械行业、表面防腐、防锈处理、石油化工、制药工业、印刷工业、涂料装饰业等行业排放废气中的主要污染物。该类有机物大多具有毒性，其大量排放会对环境产生严重的影响，同时也严重危害人体健康，可造成急性或慢性中毒，甚至致癌和突变。苯乙烯是无色透明油状液体，具有强挥发性，为可疑致癌物。目前，常用的VOCs控制技术有吸附法、吸收法、冷凝法、燃烧法以及膜分离法、生物法、光分解法、电晕法、等离子体法等或者上述方法的组合。其中催化燃烧法是利用催化剂的深度催化氧化活性将有机组分在燃点以下的温度(200～400℃)与氧反应，生成无毒无害的CO2和H2O，被认为是去除VOCs较为有效的方法本文档来自技高网...

【技术保护点】
负载型催化燃烧催化剂，其特征在于由载体和负载于载体上的活性组分组成，；所述活性组分由氧化铜、三氧化钼和铜钼混合氧化物组成；其中活性组分中Cu与Mo摩尔比为1:0.5‑1:4；所述活性组分负载质量占载体质量的5％‑20％。

【技术特征摘要】
1.负载型催化燃烧催化剂，其特征在于由载体和负载于载体上的活性组分组成，；所述活性组分由氧化铜、三氧化钼和铜钼混合氧化物组成；其中活性组分中Cu与Mo摩尔比为1:0.5-1:4；所述活性组分负载质量占载体质量的5％-20％。2.根据权利要求1所述的负载型催化燃烧催化剂，其特征在于所述的载体为Al2O3、分子筛、TiO2、堇青石蜂窝陶瓷载体或Al2O3-TiO2复合载体。3.一种制备如权利要求1所述的负载型催化燃烧催化剂的方法，其具体步骤如下：(1)将载体进行破碎，筛选出16～30目颗粒作为催化剂载体，清洗干燥后备用；(2)将Cu(NO3)2·3H2O和(NH4)6Mo7O24·4H2O按照Cu与Mo摩尔比...

【专利技术属性】
技术研发人员：徐炎华，钱红雅，刘志英，李溪，
申请(专利权)人：南京工业大学，
类型：发明
国别省市：江苏,32