本发明专利技术公开了一种负离子被，包括被套和被芯，所述被芯被包覆在被套内，其技术方案要点是，所述被套由两层纯棉面料制成，其三边缝制，另一边设置有可拆组件；所述被芯由负离子改性聚酯纤维、负离子改性腈纶纤维和竹炭纤维混合而成。其具有使用舒适、不易板结、能抑制虫螨滋生的优势。本发明专利技术的另一目的是提供一种上述负离子被的制造方法。

A negative ion and its manufacture method

The invention discloses a negative ion is included, quilt cover and core, the core is encapsulated in the quilt cover, the main points of the technical proposal is that the quilt is composed of two layers of cotton fabric, third edge sewing, the other side is provided with a detachable assembly; the core is composed of anion modified polyester fiber negative ion modified acrylic fiber and bamboo fiber blended. It has the advantages of comfortable use, not easy to knot, and can inhibit the breeding of insects and mites. Another purpose of the present invention is to provide a method for making the negative ions of the above mentioned.

【技术实现步骤摘要】
一种负离子被及其制造方法
本专利技术涉及一种负离子被及其制造方法。
技术介绍
被子是床上用品的一种，一般用作睡眠时保暖。被子通常由被套或者被单包着棉絮而成，用棉做的被子叫做棉被。除棉被外，还有羊毛被、蚕丝被、羽绒被等不同种类。现有申请公布号为CN102078109A的中国专利本专利技术公开了一种被子，其为层状结构，所述层状结构自上而下依次为羊毛层、纤维层、蚕丝层、纤维层和羊毛层。但是，羊毛、蚕丝和纤维素纤维均是天然纤维，具有良好的吸湿性，用其制作被子长期使用容易吸潮，造成被芯板结，不仅影响被子使用的舒适性，还容易滋生细菌、螨虫，不利于人体健康。
技术实现思路
针对现有技术存在的不足，本专利技术的目的在于提供一种负离子被，其具有使用舒适、不易板结、能抑制虫螨滋生的优势。为实现上述目的，本专利技术提供了如下技术方案：一种负离子被，包括被套和被芯，所述被芯被包覆在被套内，所述被套由两层纯棉面料制成，其三边缝制，另一边设置有可拆组件；所述被芯由负离子改性聚酯纤维、负离子改性腈纶纤维和竹炭纤维混合而成。通过采用上述技术方案，聚酯纤维和腈纶纤维均是化学纤维，强力好、耐磨，且不易吸水，采用其作为被芯的本文档来自技高网...

【技术保护点】
一种负离子被，包括被套(1)和被芯(2)，所述被芯(2)被包覆在被套(1)内，其特征在于：所述被套(1)由两层纯棉面料制成，其三边缝制，另一边设置有可拆组件(4)；所述被芯(2)由负离子改性聚酯纤维、负离子改性腈纶纤维和竹炭纤维混合而成。

【技术特征摘要】
1.一种负离子被，包括被套(1)和被芯(2)，所述被芯(2)被包覆在被套(1)内，其特征在于：所述被套(1)由两层纯棉面料制成，其三边缝制，另一边设置有可拆组件(4)；所述被芯(2)由负离子改性聚酯纤维、负离子改性腈纶纤维和竹炭纤维混合而成。2.根据权利要求1所述的一种负离子被，其特征在于：所述被芯(2)中负离子改性聚酯纤维、负离子改性腈纶纤维和竹炭纤维的重量比为5:3:2。3.根据权利要求2所述的一种负离子被，其特征在于：所述被芯(2)外套设有网套(3)，所述负离子改性聚酯纤维、负离子改性腈纶纤维和竹炭纤维被包覆在网套(3)内。4.根据权利要求3所述的一种负离子被，其特征在于：所述网套(3)由涤纶线编织而成，其目数为10-35目。5.根据权利要求4所述的一种负离子被，其特征在于：所述可拆组件(4)为按扣或者尼龙粘扣。6.一种如权利要求5所述的负离子被的制造方法，其特征在于：包括如下步骤...

【专利技术属性】
技术研发人员：张学新，
申请(专利权)人：南通优棉濠晨纺织品有限公司，
类型：发明
国别省市：江苏,32