皮辊轴承胶辊的衬套材料制造技术
Roller bearing roller bushing materials
Liner material of the invention relates to a roller bearing roller, which belongs to the technical field of textile machinery and equipment manufacturing. It is made up of a steel bushing and a rubber roll, and the material of the steel bushing is 08F. The 08F material is cold drawn into a tube with a length and diameter. The glued rubber is glued on the 08F pipe, and the finished rubber roller is cut off and the necessary later stage is made to form the finished product of the spinning cots. The invention has the advantages of good guide, strong stability, excellent comprehensive mechanical performance and so on.
【技术实现步骤摘要】
皮辊轴承胶辊的衬套材料
本专利技术涉及一种皮辊轴承胶辊的衬套材料，属于纺织机械器材制造
技术介绍
随着新材料、新工艺在纺织领域不断地推广应用，一种只拥有微量套差的铝衬胶辊，已得到所有纺织厂的认可并全面使用。这种胶辊的结构是：在橡胶辊的孔部，胶合了一层合金铝衬套，以此作为与上罗轴承外壳外圆过盈连接的衬。它的特点是：合金铝衬套的孔与轴承外壳外圆之间的过盈量小（一般为0.06mm），因而其不影响胶辊本身所拥有的弹性，最大程度地满足了纺纱牵伸钳口上的弹性需要，故而对提高纺纱的成纱质量有着显著作用。但是，这种胶辊的铝衬套强度较低，抗形变能力不足。在实际使用中尽管其铝衬套的孔与轴承外壳外圆之间的过盈量很小，但两者之间的套制还却十分困难，具体表现为：轴承的外角啃划铝衬内壁；铝衬产生椭圆形变等。究其原因是由于金属铝的塑性大、强度低，造成导向性能不好所产生的。
技术实现思路
本专利技术的目的在于提供一种皮辊轴承胶辊的衬套材料，旨有提高胶辊衬套的强度和抗形变能力。为了实现上述目的，本专利技术的技术方案是：它由钢衬套与橡胶辊构成，所述钢衬套的材料为08F。将08F材冷拉成一定长度与孔径的管；在08F管上热胶合橡胶；切断成钢衬胶辊，再进行必要的后期制作形成纺纱用胶辊的成品。本专利技术具有套制导向性好、稳定性强、综合机械性能优越等优点。附图说明附图1为本专利技术的结构示意图。在附图1中：1钢衬套、2橡胶辊。具体实施方式如附图1所示，选用08F作为本专利技术中钢衬套1的原材料。将08F材冷拉成指定规格长度、指定外径和内径的管；在08F管上热胶合成型丁晴橡胶辊2；切断钢衬胶辊的毛...
【技术保护点】
一种皮辊轴承胶辊的衬套材料，它由钢衬套与橡胶辊构成，其特征在于所述钢衬套的材料为08F。
【技术特征摘要】
1.一种皮辊轴承胶辊的衬套材料，它由钢衬套与橡...