The present invention relates to an improved artificial quartz stone plate, according to the weight fraction ratio by the following components: made of quartz particles 77 97; mixture 32 49; 71 water reducing agent 82; coupling agent 3 6; unsaturated resin 6 23; 0.3 pigment 6; 32 pieces of plastic 58; methyl ethyl ketone peroxide 0.8 2; 16 quartz powder 32 copies; 0.5 copies of 0.35 additives. The invention has the advantages that the artificial quartz stone plate of the invention has high impact toughness, solves the problem of artificial quartz stone cracking, deformation and so on, the product of the invention, in the test, using 1kg solid steel ball from the height of free fall impact specifications above 200cm 250mm*250mm* 15mm central plate, not cracking.
【技术实现步骤摘要】
一种改进型人造石英石板材
本专利技术涉及石板领域,特别涉及一种改进型人造石英石板材。
技术介绍
人造石英石属于脆性高分子复合材料,其具有极强的耐酸、耐腐蚀、耐磨损、耐高温等特性。现有技术制造人造石英石的配方主要是石英石、石英粉和树脂搭配经硬化成型后形成。因人造石英石同时还具有热胀冷缩的特性,存在着一定的收缩应力、冲击韧性、断裂伸长率等力学性能,目前生产人造石英的配方及技术所制造的人造石英石还存在着一些缺陷,特别是冲击韧性不佳,当材料承受因热胀冷缩带来的内应力,或受到的外部撞击力时,材料容易出现开裂、变形。因此,有必要提供一种具有高冲击韧性、不易开裂变形的人造石英石板材。
技术实现思路
本专利技术要解决的技术问题是提供一种不易出现开裂、变形的改进型人造石英石板材。为解决上述技术问题,本专利技术的技术方案为:一种改进型人造石英石板材,其创新点在于:按重量分数配比由以下组分制成:石英颗粒77-97份;混合料32-49份;减水剂71-82份;偶联剂3-6份;不饱和树脂6-23份;颜料0.3-6份;塑料碎片32-58份;过氧化甲乙酮0.8-2份;石英粉16-32份;助剂0.35-0.5份。进一步的,所述不饱和树脂为不饱和聚酯树脂。进一步的,所述的助剂为硅烷偶联剂和过氧化-2-乙基己酸叔丁酯的混合物,所述硅烷偶联剂和过氧化-2-乙基己酸叔丁酯的重量比例为4∶1。本专利技术的优点在于:本专利技术的石材配方,本专利技术的人造石英石板材具有高抗冲击韧性,解决了人造石英石开裂、变形等问题,本专利技术的产品,在测试中,用1kg实心钢球从200cm以上的高度自由下落冲击规格为250m ...
【技术保护点】
一种改进型人造石英石板材,其特征在于:按重量分数配比由以下组分制成:石英颗粒 77‑97份;混合料 32‑49份;减水剂 71‑82份;偶联剂 3‑6份;不饱和树脂 6‑ 23份;颜料 0.3 ‑ 6份;塑料碎片 32‑58份;过氧化甲乙酮 0.8‑2份;石英粉 16‑32份;助剂 0.35 ‑ 0.5 份。
【技术特征摘要】
1.一种改进型人造石英石板材,其特征在于:按重量分数配比由以下组分制成:石英颗粒77-97份;混合料32-49份;减水剂71-82份;偶联剂3-6份;不饱和树脂6-23份;颜料0.3-6份;塑料碎片32-58份;过氧化甲乙酮0.8-2份;石英粉16-32份;助剂0.35-0....
【专利技术属性】
技术研发人员:沈建美,
申请(专利权)人:南通戈雅石业有限公司,
类型:发明
国别省市:江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。