一种石墨烯土聚水泥及其制备方法技术

本发明专利技术公开了一种石墨烯土聚水泥，包括按质量比计的偏高岭土100份、氢氧化钠10份、水玻璃40份、水30份、填充剂0.6～1份和分散剂1～4份，所述填充剂包括PVA纤维，所述分散剂包括石墨烯。其抗压强度为31～41MPa，抗折强度为4.2～6.2MPa。该石墨烯土聚水泥以偏高岭土、氢氧化钠、水玻璃以及水作为土聚水泥的主要原料，将石墨烯分散剂、PVA纤维按照不同的量加入土聚水泥以提高其强度以及其工作性能，使之作为3D打印建筑材料。

A kind of graphene soil cement and its preparation method

The invention discloses a graphene soil cement, including 100 parts of metakaolin, 10 parts of sodium hydroxide, 40 parts of water glass, 30 parts of water, 0.6 to 1 parts of filler and 1~4 parts of dispersing agent according to mass ratio meter, and the filler comprises PVA fiber, and the dispersing agent comprises graphene. The compressive strength is 31 ~ 41MPa, and the flexural strength is 4.2 ~ 6.2MPa. The graphene geopolymeric cement with metakaolin, sodium hydroxide, water glass and water as the main raw material of geopolymeric cement, graphene dispersant, PVA fiber with different amount of cement to improve its strength and work performance, so as 3D printing materials.

【技术实现步骤摘要】
一种石墨烯土聚水泥及其制备方法
本专利技术涉及固定建筑物基础
，特别是一种石墨烯土聚水泥及其制备方法。
技术介绍
土聚水泥是以偏高岭土(高岭土经600-900℃煅烧)和碱激发剂为主要原料，通过化学反应所得到的新型胶凝材料。在矿物组成上完全不同于硅酸盐水泥，其主要由无定形矿物组成：①高活性偏高岭土；②碱性激活剂(氢氧化钠，水玻璃等)；③外加剂(主要有缓凝剂等)。土聚水泥各种性能优于普通硅酸盐水泥，力学性能好，耐腐蚀性强，耐久性良好，耐高温，CO2排放低，并且具有快硬早强的性能。
技术实现思路
本专利技术旨在提供一种较现有产品具有更高强度的土聚水泥。同时早期强度明显提高。一种石墨烯土聚水泥，包括按质量比计的偏高岭土100份、氢氧化钠10份、水玻璃40份、水30份、填充剂0.6～1份和分散剂1～4份，所述填充剂包括PVA纤维，所述分散剂包括石墨烯。所述石墨烯土聚水泥抗压强度为31～41MPa，抗折强度为4.2～6.2MPa。还公开了上述石墨烯土聚水泥的制备方法，包括：偏高岭土的烧制：将高岭土以600～800℃煅烧1～4小时，随后保温1～4小时，取出后冷却至室温；碱性激发剂的配制：将氢氧化本文档来自技高网...

【技术保护点】
一种石墨烯土聚水泥，其特征在于：包括按质量比计的偏高岭土100份、氢氧化钠10份、水玻璃55份、水30份、填充剂0.6～1份和分散剂1～4份，所述填充剂包括PVA纤维，所述分散剂包括石墨烯。

【技术特征摘要】
1.一种石墨烯土聚水泥，其特征在于：包括按质量比计的偏高岭土100份、氢氧化钠10份、水玻璃55份、水30份、填充剂0.6～1份和分散剂1～4份，所述填充剂包括PVA纤维，所述分散剂包括石墨烯。2.根据权利要求1所述的石墨烯土聚水泥，其特征在于：所述石墨烯土聚水泥抗压强度为31～41MPa，抗折强度为4.2～6.2MPa。3.一种石墨烯土聚水泥的制备方法，包括以下步...

【专利技术属性】
技术研发人员：张国学，卢娟，
申请(专利权)人：佛山科学技术学院，
类型：发明
国别省市：广东,44