一种大功率PIN开关组件的混合激光焊接封盖的方法技术

本发明专利技术公开了一种大功率PIN开关组件的混合激光焊接封盖的方法，包括预焊步骤：固定焊接件，以多点融合的模式采用脉冲波形技术焊接形成焊缝，此时的焊缝的状态一致性较高；复焊步骤：采用连续波形技术对预焊的焊缝使用连续输出的激光进行加强。该方法采用脉冲波形技术进行预焊形成一致性较高的焊缝后，采用连续波形技术进行复焊，复焊良率提升，大大的降低了产品的报废率。

A hybrid laser welding seal for a high power PIN switch module

The invention discloses a method for hybrid laser power PIN switch assembly welding sealing, including pre welding steps: fixed welding parts, with multi point fusion mode by pulse waveform welding technology to form weld seam at the state of high consistency; complex welding steps: using continuous wave technology for welding seam the use of laser output continuously strengthened. The pulse waveform technology is used for pre welding to form a consistent weld. After continuous wave technology is used to re weld, the yield is increased and the rejection rate is greatly reduced.

【技术实现步骤摘要】
一种大功率PIN开关组件的混合激光焊接封盖的方法
本专利技术涉及焊接
，具体涉及一种大功率PIN开关组件的混合激光焊接封盖的方法。
技术介绍
申请号为201520483918.6的专利公开了一种微波大功率单刀多掷PIN开关，该PIN开关的焊接现有技术采用连续波形技术激光焊接或者脉冲波形技术激光焊接。其焊接效果对比如表1所示，产品效果分别见图1、图2所示。表1序号特性项目连续波脉冲波1焊点外观鱼鳞纹光滑焊缝2焊接件升温幅度小大3焊缝宽度可控性高低4激光输出功率要求≥300W150～300W5焊接路径速度慢快6焊缝首尾功率控制无渐近渐出由上表可以看出，使用连续波形技术激光焊接，对焊接件兼容性较高，但焊缝美观程度不足，长期可靠性相对较弱，不能满足产品关于气密的要求，且报废率高。使用脉冲波技术焊接，焊缝美观，焊接结构可靠性好，能够满足长期气密的要求，但该技术对焊接件表面清洁度、表面处理状态一致性及结构尺寸精度控制要求非常高，焊接过程热效应明显，实际生产报废率较高。
技术实现思路
本专利技术为了解决上述技术问题提供一种大功率PIN开关组件的混合激光焊接封盖的方法。本专利技术通过下述技术方案实本文档来自技高网...

【技术保护点】
一种大功率PIN开关组件的混合激光焊接封盖的方法，其特征在于，包括以下步骤：预焊步骤：固定焊接件，以多点融合的模式采用脉冲波形技术焊接形成焊缝；复焊步骤：采用连续波形技术对预焊的焊缝使用连续输出的激光进行加强。

【技术特征摘要】
1.一种大功率PIN开关组件的混合激光焊接封盖的方法，其特征在于，包括以下步骤：预焊步骤：固定焊接件，以多点融合的模式采用脉冲波形技术焊接形成焊缝；复焊步骤：采用连续波形技术对预焊的焊缝使用连续输出的激光进行加强。2.根据权利要求1所述的一种大功率PIN开关组件的混合激光焊接封盖的方法，其特征在于，还包括预焊检验步骤：检查初焊的焊缝，若焊缝有缩边、弹坑现象，则挑出该焊接件，重复预焊步骤至焊缝无缩边、弹坑现象。3.根据...