The invention relates to a negative ion putty powder, which is mainly composed of the weight of raw materials: heavy calcium carbonate powder 750 850; 120 sierozem 180; white cement 40 60; palygorskite clay 2.5 3.5; bagasse fiber 3 8; hydroxypropyl methyl cellulose 0.5 1; 5 natural resin 10; sodium alginate 2.5 3.5; 5 iron magnesium tourmaline 10; nano terbium oxide 3 HPMC3.5 5; 5.5; 0.9 and 0.6 ultramarine blue peony powder 2 4; putty powder has the versatility, cost low, high strength, good water resistance, whiteness etc.; Chinese medicine ingredients contain peony putty powder, peony volatile ingredients can treat insomnia, containing the peony peony putty powder can emit aroma, but also prevent insomnia and tranquilizing health effects, application The decoration of the bedroom.
【技术实现步骤摘要】
一种负离子腻子粉
本专利技术涉及建筑工程领域,尤其涉及一种负离子腻子粉。
技术介绍
腻子粉是漆类施工前,对施工面进行预处理的一种表面填充材料,主要目的是填充施工面的孔隙及矫正施工面的曲线偏差,为获得均匀、平滑的漆面打好基础。我们国家的标准,将成品腻子分为:一般型腻子和耐水型腻子。一般型腻子用于不要求耐水的场所。由双飞粉、淀粉胶、纤维素组成。耐水型腻子用于要求耐水、高粘结强度的场所。由双飞粉、灰钙粉、水泥、有机胶粉、保水剂等组成。具耐水性、耐碱性、粘结强度。无论是一般型腻子还是耐水型腻子其缺点是通用性差,一般型腻子由于不耐水,只能由于客厅等室面装置,耐水性腻子粉虽然耐水性好,但白度和质感不够,一般只用于卫生间。针对现有腻子粉通用性差、强度低等问题,本申请人研制了一种通用性较高的标准型腻子粉,已解决上述问题。
技术实现思路
本专利技术要解决的技术问题是提供一种负离子腻子粉,具有强度高、防水、白度高等优点,进而解决了现有腻子粉通用性差的问题。为解决上述技术问题,本专利技术的技术方案为:一种负离子腻子粉,其创新点在于:它主要由下述重量份的原料组成:重质碳酸钙粉750-850份;灰钙粉120-180份;白水泥40-60份;坡缕石粘土2.5-3.5份;甘蔗渣纤维3-8份;羟丙基甲基纤维素0.5-1份;天然树脂5-10份;海藻酸纳2.5-3.5份;铁镁电气石5-10份;纳米铽氧化物3-5份;HPMC3.5-5.5份;群青0.6-0.9份和芍药粉2-4份。本专利技术的优点在于:1)本专利技术的腻子粉,具有通用性强、成本低、强度高、耐水性好、白度高等优点,本专利技术的腻子粉在适 ...
【技术保护点】
一种负离子腻子粉,其特征在于:它主要由下述重量份的原料组成 : 重质碳酸钙粉 750‑850份;灰钙粉 120‑180份;白水泥 40‑60份 ; 坡缕石粘土2.5‑3.5 份;甘蔗渣纤维3‑8份;羟丙基甲基纤维素0.5‑1 份 ;天然树脂5‑10份;海藻酸纳2.5 ‑3.5份;铁镁电气石5‑10份;纳米铽氧化物3‑5份;HPMC3.5‑5.5份;群青0.6‑0.9份和芍药粉2‑4份。
【技术特征摘要】
1.一种负离子腻子粉,其特征在于:它主要由下述重量份的原料组成:重质碳酸钙粉750-850份;灰钙粉120-180份;白水泥40-60份;坡缕石粘土2.5-3.5份;甘蔗渣纤维3-8份...
【专利技术属性】
技术研发人员:蒋左清,
申请(专利权)人:江苏昶浩建材有限公司,
类型:发明
国别省市:江苏,32