The present invention discloses a high refractive index sulphur containing polymer and its preparation method and application, which belongs to the field of polymer optical materials. Sulfur containing polymers with high refractive index of the type I or II, has shown the structure; the invention of containing three triazine compounds or silane monomer as raw material of mercapto carboxylic acid ester monomer, allyl containing, prepared by thermal curing sulfur-containing polymers with high refractive index, the preparation process is simple, sulfur containing polymers prepared by refraction rate, good mechanical properties, has higher application value in optical lens, LED packaging materials and so on.
【技术实现步骤摘要】
一种高折射率的含硫聚合物及其制备方法与应用
本专利技术属于高分子光学材料领域，具体涉及一种高折射率的含硫聚合物及其制备方法与应用。
技术介绍
高折射率光学树脂材料可以减少透镜的厚度，减轻质量，实现透镜的轻量化和小型化。目前，高折射率光学树脂材料主要包括环氧树脂类(折射率1.5～1.6)、聚硅氧烷类(折射率1.5～1.6)、聚氨酯类(折射率1.55～1.65)、含硫聚合物类(折射率1.6～1.7)、聚酰亚胺类(折射率1.65～1.75)等。在光学材料分子结构中引入具有高摩尔折射率数值的基团，如硫元素、除氟以外的卤素(溴、碘)、芳环以及金属元素有利于提高材料的折射率。同时还必须考虑到材料的透明性以及加工性能，因此，引入硫元素以及芳杂环是提高聚合物光学材料折射率较为理想的途径。作为光学材料的含硫聚合物中硫元素通常以环硫、硫酯键、硫醚键、砜基等形式存在，从含硫聚合物化学结构上可分为含硫环氧树脂类、含硫聚氨酯类、含硫聚酰亚胺类等。中国专利CN101665552A提供了一种含硫聚合物光学树脂，由六种不同组分的单体材料制备而成，结构复杂，其折射率1.6左右。中国专利CN1016...
【技术保护点】
一种高折射率的含硫聚合物，其特征在于：该含硫聚合物具有式Ⅰ或Ⅱ所示结构：
【技术特征摘要】
1.一种高折射率的含硫聚合物，其特征在于：该含硫聚合物具有式Ⅰ或Ⅱ所示结构：其中，n为5～100。2.权利要求1所述的高折射率的含硫聚合物的制备方法，其特征在于包含如下步骤：以含巯基羧酸酯单体、含烯丙基的三嗪类或硅烷类化合物单体作为原料，通过热固化法制备得到高折射率的含硫聚合物。3.根据权利要求2所述的高折射率的含硫聚合物的制备方法，其特征在于：所述的含巯基羧酸酯单体为季戊四醇四巯基乙酸酯、季戊四醇四(3-巯基丙酸)酯、季戊四醇四(4-巯基)苯甲酸酯、三羟甲基丙烷三(2-巯基乙酸)酯、三羟甲基丙烷三(3-巯基丙酸)酯和三羟甲基丙烷三(4-巯基)苯甲酸酯中的至少一种。4.根据权利要求2所述的高折射率的含硫聚合物的制备方法，其特征在于：所述的含烯丙基的三嗪类或硅类化合物单体为1,3,5-三-2-丙烯基-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮、1,3,5-三丙烯酰基六氢-1,3,5-三嗪、1,3,5-三丙烯酰基六氢-1,3,5-三嗪、四烯丙基硅烷和四烯丙基锡中的至少一种。5.根据权利要求2所述的高折射率的含硫聚合物的制备方法，其特征在于：所述的原料...