The invention provides a manufacturing method of plant straw pot, the method uses simple equipment, less investment, low production cost, the production of straw pot seedling or sapling transplantation as easy to use, plant roots and interludes, disintegrating into high-quality organic fertilizer, beneficial to plant growth. In this method, plant straw as the main raw material, adding alkaline solution the raw pH value rose to more than 9, composting softening after crushing, grinding after adding acid solution to adjust the pH value to the neutral range, then add uniform mixing, pressing and forming, demoulding and drying production process, the amount of weight ratio plant straw: alkaline solution, acid solution: add material = 1: (0.2 ~ 0.6): (0.06 ~ 0.2): (0.02 ~ 0.08). It is suitable for container seedling raising and pot culture.
【技术实现步骤摘要】
一种植物秸秆盆钵的制造方法
本专利技术涉及一种植物栽培盆钵的制造方法，适应于容器育苗与盆钵栽培，属于秸秆资源化利用以及植物栽培盆钵制造的工艺方法。
技术介绍
植物秸秆作为一种再生资源，每年全国仅农作物秸秆产生量达六亿吨，在农村能源供应短缺的年代，秸秆主要作为燃料被利用消耗，然而，近年随着农村新型能源，如：沼气、煤气、天然气等应用，加之农作物秸秆产量的提高，秸秆出现大量过剩，因秸秆田头焚烧或随意遗弃给空气、水体、农村等环境造成污染的现象越来越严重。因此，寻求秸秆处置的新技术、新途径十分重要。在蔬菜、棉花、林木、花卉等植物的栽培方法中，容器育苗具有根系完整，四季可移栽，成活率高，抗逆性强等一系列优点。寻求满足制造育苗容器要求的新材料与新工艺意义重大。在花卉栽培中，特别是草花栽培中，可反复使用或再生利用的盆钵，不仅可节约成本，且可减少因破碎盆钵处置而造成的费用或环境负担。
技术实现思路
本专利技术针对秸秆加工制作育苗容器存在的缺点，提供一种植物秸秆盆钵的制造方法，该方法使用的设备简单、投资少、生产成本低，生产的秸秆盆钵作为育苗或树苗移植使用，易于植物根系穿插，且崩解后，成优...
【技术保护点】
一种植物秸秆盆钵制造的方法，其特征是以植物秸秆为主要 原料，加入碱性溶液使原料pH值上升到9以上，堆制软化后进行粉 碎，粉碎后加入酸性溶液调节pH值至中性范围，再加入添料混合均 匀，经压制成型、脱模干燥工序制作而成，其用量的重量比为植物秸 秆∶碱性溶液∶酸性溶液∶添料＝1∶(0.2～0.6)∶(0.06～0.2)∶(0.02～ 0.08)。
【技术特征摘要】
1.一种植物秸秆盆钵制造的方法，其特征是以植物秸秆为主要原料，加入碱性溶液使原料pH值上升到9以上，堆制软化后进行粉碎，粉碎后加入酸性溶液调节pH值至中性范围，再加入添料混合均匀，经压制成型、脱模干燥工序制作而成，其用量的重量比为植物秸秆∶碱性溶液∶酸性溶液∶添料＝1∶(0.2～0.6)∶(0.06～0.2)∶(0.02～0.08)。2.根据权利要求1所述的植物秸秆盆钵制造的方法，其特征在于所述加碱液溶液为浓度为1～5％的氢氧化钾或5～15％的石灰水或碳酸盐溶液。3.根据权利要求1所述的植物秸秆盆钵制造的方法，其特征在于所述酸性溶液为废硫酸溶液或磷酸溶液。4.根据权利要求1所述的植物秸秆盆钵制造的方法，其特征在于所述添料为粘结剂、吸水剂或植物营养剂，或三者的任意组合。5.根据权利要求4所述的植物秸秆盆钵制造的方法，其特征在于所述粘合剂为...