The invention provides a method for using calcium chloride / ethanol / water solution method for preparing fluorescent silk fabric, the method comprises the following steps: (1) the solution preparation of molar ratio of 1:2:8: preparation of calcium chloride / ethanol / water solution to, and then added phosphor nanoparticles obtained under ultrasonic oscillation a solution of phosphor nanoparticles dispersed; (2) the silk fabric in step (1) solution obtained in multiple padding; (3) the padding after the silk fabric was steaming; (4) the steam after the silk fabric was immersed in methanol solution and solidification. Washing and drying. The preparation technology is simple and easy, the cost is low, the strength of the silk fabric is small, and the surface property of the silk fiber is not changed, and the fluorescent powder nano particle has good fastness on the silk fabric; no adhesive is used in the preparation process, and the toxicity is harmless.
【技术实现步骤摘要】
用氯化钙/乙醇/水溶液制备荧光蚕丝织物
本专利技术涉及一种功能织物的制备方法，尤其是一种使用氯化钙/乙醇/水溶液制备荧光蚕丝织物的方法。
技术介绍
将纳米粒子引入纺织纤维中，可以制备得到功能性纤维材料。目前将纳米粒子引入蚕丝纤维的制备方法很多，如：吸附法，溶胶凝胶法，层层组装法，涂层法，喂食法等。然而，吸附法通过主要通过分子间范德华力和离子键力使纳米粒子吸附到蚕丝纤维表面，水洗牢度较低；溶胶凝胶法和层层组装法的工艺过程较长，且较难控制；涂层法是利用粘合剂将纳米粒子粘合到蚕丝纤维表面，降低了蚕丝纤维对人体的亲肤性；喂食法是将纳米粒子混入家蚕食物中，使蚕丝纤维混入纳米粒子，缺点是效率很低。氯化钙/乙醇/水溶液（摩尔比为1:2:8），是溶解丝素最为常用的溶剂，当氯化钙，乙醇，水的摩尔比为1:2:8时，三元溶液对丝素的溶解能力最好，且不会引起丝素大分子链的严重降解。三元溶剂中的氯化钙与丝素中的酪氨酸发生作用，消弱丝素分子之间的范德华力和氢键。
技术实现思路
本专利技术所要解决的技术问题是，针对以上现有技术存在的缺点，提出一种使用氯化钙/乙醇/水溶液制备荧光蚕丝织物的方法。该制...
【技术保护点】
一种使用氯化钙/乙醇/水溶液制备荧光蚕丝织物的方法，其特征在于，包括如下步骤：（1）溶解液的制备：按照摩尔比1:2:8制备氯化钙/乙醇/水溶液，然后在其中加入荧光粉纳米粒子，超声振荡下得到分散有荧光粉纳米粒子的溶解液；（2）将蚕丝织物在步骤（1）所得的溶解液中多次浸轧；（3）将浸轧后的蚕丝织物在100‑120℃下汽蒸5‑30min；（4）将汽蒸后的蚕丝织物浸渍于甲醇溶液中凝固，然后水洗、烘干。
【技术特征摘要】
1.一种使用氯化钙/乙醇/水溶液制备荧光蚕丝织物的方法，其特征在于，包括如下步骤：（1）溶解液的制备：按照摩尔比1:2:8制备氯化钙/乙醇/水溶液，然后在其中加入荧光粉纳米粒子，超声振荡下得到分散有荧光粉纳米粒子的溶解液；（2）将蚕丝织物在步骤（1）所得的溶解液中多次浸轧；（3）将浸轧后的蚕丝织物在100-120℃下汽蒸5-30min；（4）将...