本发明专利技术提供了一种脱色滤纸及其制备方法。本发明专利技术提供的脱色滤纸包含涤纶双组份纤维和阳离子改性的纤维素纤维，所述涤纶双组份纤维和阳离子改性的纤维素纤维的质量比为(15～40):(60～85)。本发明专利技术提供的脱色滤纸采用涤纶双组份纤维和阳离子改性的纤维素纤维作为原料组分，并且严格控制两种纤维的质量比例，得到的滤纸在具有过滤功能的基础上，同时还具有优异的脱色性能，能够同时实现过滤和脱色，减少生产工序、节约成本、节省时间。

Decoloring filter paper and preparation method thereof

The present invention provides a decolorizing filter paper and its preparation method. The decolorizing filter paper provided by the invention comprises a polyester two-component fiber and a cationic modified cellulose fiber, and the mass ratio of the polyester two-component fiber and the cationic modified cellulose fiber is (15~40): (60~85). Decolorization of filter paper provided by the invention adopts polyester bicomponent fibers and cationic modified cellulose fiber as raw material components, and strictly control the quality of the proportion of two kinds of fibers, the filter based on with filtering function, but also has excellent decolorizing performance, can simultaneously achieve filtering and decolorizing, reduce the production processes save cost and save time.

【技术实现步骤摘要】
一种脱色滤纸及其制备方法
本专利技术涉及滤纸
，尤其涉及一种脱色滤纸及其制备方法。
技术介绍
在金属薄板加工过程中热轧油的使用量及重复利用率很高，在热轧油再循环使用过程中需要对其进行过滤以及脱色。由于现有技术中的滤纸一般只有过滤作用，基本不具备脱色功能。因此，在金属板加工过程中需要进行两道程序：过滤工序和脱色工序，工序复杂，浪费人力和物力。
技术实现思路
本专利技术的目的在于提供一种脱色滤纸及其制备方法，本专利技术提供的脱色滤纸在保证滤纸的过滤功能的基础上，同时还具有优异的脱色性能，能够同时实现过滤和脱色，减少生产工序、节约成本、节省时间。为了实现上述专利技术目的，本专利技术提供以下技术方案：本专利技术提供了一种脱色滤纸，包含涤纶双组份纤维和阳离子改性的纤维素纤维，所述涤纶双组份纤维和阳离子改性的纤维素纤维的质量比为(15～40):(60～85)。优选的，所述涤纶双组份纤维和阳离子改性的纤维素纤维的质量比为(20～30):(70～80)。优选的，所述涤纶双组份纤维和阳离子改性的纤维素纤维的细度独立的为1～4D。优选的，所述涤纶双组份纤维和阳离子改性的纤维素纤维的长度独立的为35～5本文档来自技高网...

【技术保护点】
一种脱色滤纸，包含涤纶双组份纤维和阳离子改性的纤维素纤维，所述涤纶双组份纤维和阳离子改性的纤维素纤维的质量比为(15～40):(60～85)。

【技术特征摘要】
1.一种脱色滤纸，包含涤纶双组份纤维和阳离子改性的纤维素纤维，所述涤纶双组份纤维和阳离子改性的纤维素纤维的质量比为(15～40):(60～85)。2.根据权利要求1所述的脱色滤纸，其特征在于，所述涤纶双组份纤维和阳离子改性的纤维素纤维的质量比为(20～30):(70～80)。3.根据权利要求1所述的脱色滤纸，其特征在于，所述涤纶双组份纤维和阳离子改性的纤维素纤维的细度独立的为1～4D。4.根据权利要求1或3所述的脱色滤纸，其...