一种提高医用镁合金表面耐腐蚀及亲水性能的涂层及其制备方法技术
Coating for improving corrosion resistance and hydrophilic property of medical magnesium alloy surface and preparation method thereof
The invention provides a method for improving the corrosion resistance and the hydrophilic surface of magnesium alloy coating, Mg composite coating 74/MgF2 MOF. At the same time provides a preparation method of the composite coating, that is using hydrofluoric acid etching the magnesium alloy formed on the surface of MgF2 film, and then through the method of hydrothermal synthesis on the surface of in situ Mg MOF 74 coating surface containing magnesium alloy composite coating Mg MOF 74/MgF2 corrosion resistance to a great extent at the same time improve, also greatly improve the hydrophilic performance.
【技术实现步骤摘要】
一种提高医用镁合金表面耐腐蚀及亲水性能的涂层及其制备方法
本专利技术属于生物医用镁合金表面处理
，具体涉及一种在镁合金表面构筑Mg-MOF-74/MgF2复合涂层的方法，从而提高医用镁合金表面的耐蚀性和亲水性，实现该类复合材料在生物医学工程方面的应用。
技术介绍
镁合金密度低，比强度、比刚度高，与人体自身骨组织力学性能接近且具有生物可降解性，因此被认为是一种极具潜力的可降解医用骨植入材料。但是镁合金的耐腐蚀性极差，在人体内的降解速度与组织愈合速度不匹配，进而限制了镁合金在临床中的应用，因此，改善其腐蚀速率过高的问题是医用镁合金研究的重点。表面改性技术是针对镁合金降解过快问题的有效解决途径之一，除此之外，表面改性技术还能够在一定程度上改善镁合金的生物相容性。常见提高镁合金耐腐蚀性的表面涂层材料包括：生物活性玻璃、羟基磷灰石、金属氧化物、高分子聚合物及MgF2化学转化膜等，上述研究成果为医用镁合金的表面处理奠定了一定的基础。但是，大多数耐腐蚀材料表面同时具有疏水性，而疏水性的表面不利于人体细胞的吸附与增殖，尤其是在镁合金作为人体骨组织替代物的时候，耐腐蚀且亲水的...
【技术保护点】
一种提高医用镁合金表面耐腐蚀及亲水性能的涂层，其特征在于，该涂层为Mg‑MOF‑74/MgF2复合涂层。
【技术特征摘要】
2017.06.28 CN 20171050984611.一种提高医用镁合金表面耐腐蚀及亲水性能的涂层，其特征在于，该涂层为Mg-MOF-74/MgF2复合涂层。2.一种权利要求1所述的提高医用镁合金表面耐腐蚀及亲水性能的涂层的制备方法，包括以下步骤：（1）医用镁合金的表面预处理：以镁合金AZ31B作为基体材料，用砂纸打磨，用丙酮、乙醇及去离子水清洗，备用；（2）MgF2膜层的制备：将上述预处理后的镁合金片放入氢氟酸中酸蚀，使其表面产生MgF2化学转化膜，然后取出用去离子水冲洗干净，备用；（3）反应溶液的配制...
【专利技术属性】
技术研发人员：刘伟，闫志杰，耿铁，田煜，
申请(专利权)人：河南工业大学，
类型：发明
国别省市：河南,41
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。