本发明专利技术公开了一种高分子防水涂料，包括以下重量份的组分：聚氨酯20‑30份；聚乙烯醇15‑20份；邻甲基苯二酸10‑13份；环保催化剂8‑10份；乙二醇5‑8份；钛白粉3‑5份；分散剂0.1‑0.3份；松焦油6‑9份；去离子水25‑30份。本发明专利技术的有益效果是：采用环保催化剂作为该涂料的介质，能有效的提高涂料的粘附性，同时增强了防水效果，同时与其它原料相互结合，使得涂料具有优异的耐热性和抗腐蚀性，环保效果好，适用于建筑行业。

A kind of macromolecule waterproof coating

The invention discloses a polymer waterproof coating, which comprises the following components by weight: 20 to 30 polyurethane; polyvinyl alcohol 15 20; O - phthalic acid 10 13; 8 10 environmental catalyst; ethylene glycol 5 8; titanium dioxide 3 5; 0.1 dispersant 0.3; 6 pine tar 9; 25 deionized water 30. The beneficial effect of the invention is: the use of environmentally friendly catalyst as the coating medium, can effectively improve the adhesion of the coating, but also enhance the waterproof effect, while the combination with other materials, the coating has excellent heat resistance and corrosion resistance, good environmental protection effect, which is suitable for the construction industry.

【技术实现步骤摘要】
一种高分子防水涂料
本专利技术涉及一种涂料，尤其涉及一种高分子防水涂料。
技术介绍
建筑行业应用的防水涂料一般是在常温下呈无固定形状的粘稠液态高分子合成材料，涂布后经溶剂的挥发或水分的蒸发或反应固化后在基层表面形成防水膜。目前建筑行业所用的防水材料一般分为包括防水卷材、防水涂料、密封油膏等在内的柔性防水材料以及以水泥基材为主、添加防水剂及其他助剂的刚性防水材料。种类虽然丰富，但普遍具有物理力学性能差，使用寿命短、与建筑物的使用寿命差距过大，应用范围狭小，不安全环保等缺点。所以无缝防水是建筑业在世界范围内的难题，为此，人们展开了广泛的研究。因此，为解决上述问题，特提供一种新的技术方案。
技术实现思路
本专利技术提供一种高分子防水涂料。本专利技术采用的技术方案是：一种高分子防水涂料，包括以下重量份的组分：进一步的，所述环保催化剂包括高岭土、纤维素和助溶剂，所述高岭土、纤维素和助溶剂的重量百分比为2:1:0.5。进一步的，所述助溶剂为苯甲酸、苯甲酸钠或水杨酸。本专利技术的有益效果是：采用环保催化剂作为该涂料的介质，能有效的提高涂料的粘附性，同时增强了防水效果，同时与其它原料相互结合，使得涂料具本文档来自技高网...

【技术保护点】
一种高分子防水涂料，其特征在于：包括以下重量份的组分：

【技术特征摘要】
1.一种高分子防水涂料，其特征在于：包括以下重量份的组分：2.根据权利要求1所述的一种高分子防水涂料，其特征在于：所述环保催化剂包括高岭土、纤维素和助溶...

【专利技术属性】
技术研发人员：倪程凯，
申请(专利权)人：苏州卡佩罗尔高分子材料有限公司，
类型：发明
国别省市：江苏,32