The invention provides a preparation method of hydrophobic dispersion material, which relates to the field of new material technology. The preparation method of hydrophobic dispersion material includes mixing hydrophobic solid powder and surfactant, grinding and mixing with water. The preparation process is simple, controllable, and the preparation cost is low. It is suitable for large-scale production. The preparation method of hydrophobic dispersion material includes mixing hydrophobic solid powder and surfactant, grinding the first mixture, mixing water and additive into second mixture, mixing the first mixture and the second mixture. The preparation process is simple, controllable, and the preparation cost is low. It is suitable for large-scale production.
【技术实现步骤摘要】
疏水分散材料的制备方法
本专利技术涉及新材料
，且特别涉及一种疏水分散材料的制备方法。
技术介绍
疏水性固体粉末在保温材料领域、涂料领域和需要表面具有荷叶疏水效应的表面处理领域的应用越来越广。疏水性固体粉末由于具有强烈的疏水效果，和水完全不相容，无法在水中分散，需要使用溶剂才能够得到很好的分散，分散良好的疏水性固体粉末才具有实际的应用价值。但是溶剂的引入，造成了材料的挥发性有机物(VOC)超标，挥发性有机物散佚在空气中，对环境造成污染，危害人和动植物的健康。在环保要求越来越严格的今天，溶剂的使用受到空前的限制，许多溶剂型涂料和其他大量使用溶剂的配方和工艺都面临着全面停产。因此，新型分散材料受到前所未有的重视，这是今后工业发展的必然选择。
技术实现思路
本专利技术的目的在于提供一种疏水分散材料的制备方法，该方法制备工艺简单，可控性强，制备成本低，适合大规模生产。本专利技术的另一目的在于提供一种疏水分散材料的制备方法，该方法制备工艺简单，可控性强，制备成本低，适合大规模生产。本专利技术解决其技术问题是采用以下技术方案来实现的。本专利技术提出一种疏水分散材料的制备方法...
【技术保护点】
一种疏水分散材料的制备方法，其特征在于，包括：将疏水性固体粉末和表面活性剂混合、研磨，再与水混合。
【技术特征摘要】
1.一种疏水分散材料的制备方法，其特征在于，包括：将疏水性固体粉末和表面活性剂混合、研磨，再与水混合。2.根据权利要求1所述的疏水分散材料的制备方法，其特征在于，所述疏水性固体粉末、所述表面活性剂、所述水的质量比为1000:1～1000:1～100。3.一种疏水分散材料的制备方法，其特征在于，包括：将疏水性固体粉末和表面活性剂混合、研磨得第一混合物，将水与添加剂混合得第二混合物，混合所述第一混合物与所述第二混合物。4.根据权利要求3所述的疏水分散材料的制备方法，其特征在于，将所述疏水性固体粉末和所述表面活性剂采用高速混料机混合5～10分钟。5.根据权利要求4所述的疏水分散材料的制备方法，其特征在于，经过研磨的混合物的粒径小于5μm。6.根据权利要求3所述...
【专利技术属性】
技术研发人员：陈德东，雷文君，郭奂宇，
申请(专利权)人：成都硕屋科技有限公司，
类型：发明
国别省市：四川,51