The present invention relates to a pad for fitness, the fitness mat is composed of the following components in part by weight: PVC 80, TA 70 800 talcum powder 20 30, 1000 2 AC foaming agent 10, two - 1 terephthalic acid 5 ZNO, Zinc Oxide 0.1 0.5 ST, a zinc stearate 0.1 0.5, R 103 titanium dioxide 1 potassium zinc compound stabilizer 3, 0.5, 0.1 light calcium carbonate powder 0.1 0.5 copies and 3 copies of 1 masterbatch powder. The advantages of the invention are as follows: the fitness pad for the invention does not contain the glue containing benzene, is odorless and environment-friendly, and produces the leftover materials in the middle period and the retired body-building pad, which is favorable for recycling, and conforms to the general trend of energy conservation and environmental protection.
【技术实现步骤摘要】
一种健身用垫
本专利技术涉及健身用品
，特别涉及一种健身用垫。
技术介绍
随着经济的发展和人民生活水平的提高，练瑜伽成为当今社会的时尚运动之一，长期练习瑜伽可预防疾病，有效调节神经系统和内分泌系统，改善人体健康。在做瑜伽运动时要用健身用垫，健身用垫可有效减小人体与地面接触的疼痛感，健身用垫除应具有柔软和良好的回弹性等特性外，还应具备较好的防滑性能、韧性和力学性能。目前，市场上现有的双色瑜珈垫一般都是采用含苯胶水贴合，中间夹一层TC网布，由于胶水中的甲苯会残留在瑜珈垫中，容易对人类造成危害，而且退役的瑜珈垫和生产中的边角余料不易回收再利用，会对环境造成一定的不良影响，不利于环保。
技术实现思路
本专利技术要解决的技术问题是提供一种健身用垫，其不采用含苯胶水贴合，无味环保。为解决上述技术问题，本专利技术的技术方案为：一种健身用垫，其创新点在于：所述健身用垫是由以下重量份的组分组成：PVC70-80份、TA-800滑石粉20-30份、AC-1000发泡剂2-10份、对苯二甲酸二辛酯1-5份、ZNO氧化锌0.1-0.5份、ST硬脂酸锌0.1-0.5份、R-103钛白粉1...
【技术保护点】
一种健身用垫，其特征在于：所述健身用垫是由以下重量份的组分组成：PVC 70‑80份、TA‑800滑石粉20‑30份、AC‑1000发泡剂2‑10份、对苯二甲酸二辛酯1‑5份、ZNO氧化锌0.1‑0.5份、ST硬脂酸锌0.1‑0.5份、R‑103钛白粉1‑3份、锌钾复合稳定剂0.1‑0.5份、轻质碳酸钙粉0.1‑0.5份和色母粉1‑3份。
【技术特征摘要】
1.一种健身用垫，其特征在于：所述健身用垫是由以下重量份的组分组成：PVC70-80份、TA-800滑石粉20-30份、AC-1000发泡剂2-10份、对苯二甲酸二辛酯1-5份、ZNO氧化锌0.1-0.5份、ST硬脂酸锌0.1-0.5份、R-103钛白粉1-3份、锌钾复合稳定剂0.1-0.5份、轻质碳酸钙粉0.1-0.5份和色母粉1-3份。2.根据权利要求1所述的健身用垫，其特征在于：所述健身用垫是由以下重量份的组分组成：PVC74-76份、TA-800滑石粉24-26份、AC-1000发泡剂4-8...