本发明专利技术提供一种生物降解地膜，由淀粉、聚乙烯醇、纤维素、增塑剂、加工助剂组成，其配方组成成分如下：淀粉40‑60份、聚乙烯醇20‑40份、纤维素7‑10份、增塑剂3‑7份、加工助剂3‑4份，所述增塑剂为甘油与乙二醇混合物，其配比为1‑2:3‑5，所述淀粉为玉米淀粉、小麦淀粉、马铃薯淀粉中的一种，所述纤维素为甘蔗、秸秆中的一种。本发明专利技术能够在使用之后被微生物完全降解成二氧化碳和水，不会有残留，减少了环境污染，提高了农业可持续发展的可靠性。

A biodegradable mulch film

The invention provides a biodegradable plastic film composed of cellulose, starch, PVA, plasticizer, processing additives, the formula composition is as follows: 40 starch 60, polyvinyl alcohol 20 40 copies, 10 copies, 7 cellulose plasticizer 3 7 copies, 3 copies of 4 processing aids, the the plasticizer of glycerol and glycol mixture, the ratio is 1 2:3 5, the starch to corn starch, wheat starch, potato starch in one of the cellulose is a kind of sugar cane, straw in. The invention can be completely degraded into carbon dioxide and water after being used, without residue, reduced environmental pollution, and improved the reliability of agricultural sustainable development.

【技术实现步骤摘要】
一种生物降解地膜
本专利技术涉及一种农业地膜，具体涉及一种生物降解地膜。
技术介绍
农膜覆盖技术的广发应用，极大程度的促进了农业的发展，但同时对生态环境造成了极大的“白色污染”，残留在土壤里的农膜碎片也会影响作物的产量，因此，使用后能够被微生物完全降解的环保型可降解农膜成为今后农业发展的研究方向。
技术实现思路
为了解决上述技术问题本专利技术提供一种生物降解地膜，可被微生物完全分解成二氧化碳和水，杜绝了使用后的农膜对环境造成的污染。本专利技术的技术方案是：一种生物降解地膜，由淀粉、聚乙烯醇、纤维素、增塑剂、加工助剂组成，其配方组成成分如下：淀粉40-60份、聚乙烯醇20-40份、纤维素7-10份、增塑剂3-7份、加工助剂3-4份。进一步地，所述增塑剂为甘油与乙二醇混合物，其配比为1-2:3-5。进一步地，所述淀粉为玉米淀粉、小麦淀粉、马铃薯淀粉中的一种。进一步地，所述纤维素为甘蔗、秸秆中的一种。进一步地，所述配方组成成分为：淀粉50份、聚乙烯醇35份、纤维素8份、增塑剂4份、加工助剂3份。进一步地，所述配方组成成分为：淀粉55份、聚乙烯醇30份、纤维素7份、增塑剂3份、加工助剂4份。本专本文档来自技高网...

【技术保护点】
一种生物降解地膜，由淀粉、聚乙烯醇、纤维素、增塑剂、加工助剂组成，其特征在于，其配方组成成分如下：淀粉40‑60份、聚乙烯醇20‑40份、纤维素7‑10份、增塑剂3‑7份、加工助剂3‑4份。

【技术特征摘要】
1.一种生物降解地膜，由淀粉、聚乙烯醇、纤维素、增塑剂、加工助剂组成，其特征在于，其配方组成成分如下：淀粉40-60份、聚乙烯醇20-40份、纤维素7-10份、增塑剂3-7份、加工助剂3-4份。2.根据权利要求1所述的一种生物降解地膜，其特征在于，所述配方组成成分为：淀粉50份、聚乙烯醇35份、纤维素8份、增塑剂4份、加工助剂3份。3.根据权利要求1所述的一种生物降解地膜，其特征在于，所述配方组成成...