The present invention provides a polymer modified cement foundation stone, is composed of the following: the weight ratio of the raw materials of Portland cement, sulphoaluminate cement 5 15% 10 30% 0 5%, ash, gas phase SO2 0 2%, 0 3%, 20 wollastonite 100 mesh sand 15 40%, 105 300 15 mesh sand 35%, calcium carbonate 5 20%, 25%, 8 polymer materials hemihydrates 0 2%; comprehensive advantages, the invention of polymer material and cement from each other, so that the final prepared cement stone fund has excellent heat resistance, fire resistance, folding resistance, and not easy cracking, high tensile strength, no deformation, low water absorption rate, the product after the construction of beautiful and elegant appearance, excellent performance.
【技术实现步骤摘要】
一种高分子改性水泥基金磨石
本专利技术涉及建筑材料领域，具体涉及一种高分子改性水泥基金磨石。
技术介绍
水磨石是将碎石、玻璃、石英石等骨料拌入水泥粘接料制成混凝制品后经表面研磨、抛光的制品。以水泥粘接料制成的水磨石叫无机磨石，用环氧粘接料制成的水磨石又叫环氧磨石或有机磨石，水磨石按施工制作工艺又分现场浇筑水磨石和预制板材水磨石地面。其中单独使用无机产品凝胶材料具有较多不足，例如易出现开裂、抗折差、拉伸强度低等缺陷；而单独使用高分子凝胶材料也具有较多不足，例如耐温不高、变形大、防火差等。因此开发一种即可发挥水泥基、高分子等材料的优点，又可回避了他们各自缺点的高分子改性水泥基金磨石，具有广阔的市场前景。
技术实现思路
本专利技术的目的在于提供一种高分子改性水泥基金磨石，综合高分子材料与水泥基的优点，取长补短，使高分子改性水泥基金磨石综合性能优异。为实现以上目的，本专利技术通过以下技术方案予以实现：一种高分子改性水泥基金磨石，由以下重量配比的原料组成：硅酸盐水泥5-15％、硫铝酸盐水泥10-30％、灰钙粉0-5％、气相SiO20-2％、硅灰0-3％、20-100目砂15-4...
【技术保护点】
一种高分子改性水泥基金磨石，其特征在于：由以下重量配比的原料组成：硅酸盐水泥5‑15％、硫铝酸盐水泥10‑30％、灰钙粉0‑5％、气相SiO2 0‑2％、硅灰0‑3％、20‑100目砂15‑40％、105‑300目砂15‑35％、重质碳酸钙5‑20％、高分子材料8‑25％、半水石膏0‑2％。
【技术特征摘要】
1.一种高分子改性水泥基金磨石，其特征在于：由以下重量配比的原料组成：硅酸盐水泥5-15％、硫铝酸盐水泥10-30％、灰钙粉0-5％、气相SiO20-2％、硅灰0-3％、20-100目砂15-40％、105-300目砂15-35％、重质碳酸钙5-20％、高分子材料8-25％、半水石膏0-2％。2.根据权利要求1所述的高分子改性水泥基金磨石，其特征在于：所述硅酸盐水泥为白色硅酸盐水泥或黑水泥；所述白色硅酸盐水泥选自标号为425、525、625中的一种，所述黑水泥选自标号为525、625、725中的一种。3.根据权利要求1所述的高分子改性水泥基金磨石，其特征在于：所述硫铝酸盐水泥为快硬硫铝酸盐水泥、高强度硫铝酸盐水泥、膨胀硫铝酸盐水泥、低碱度硫铝酸盐水泥、自应力硫铝酸盐水泥中的一种或几种的组合。4.根据权利要求1所述的高分子改性水泥基金磨石，其...