The invention belongs to the field of preparation of coatings, in particular relates to a cement sand abrasion resistant material. Consists of the following raw materials in weight portion: 40 Portland cement 45 copies, 65 copies, 60 sand polycarboxylate 3 4 copies, 3 copies, 2 Sodium Silicate Pigment 2 4 copies, 1.5 copies, 1 silica fume polyethylene vinyl acetate copolymer 1 2 copies, 2 copies of 1 polyvinyl alcohol. The material of the invention has the advantages of high strength, good abrasion resistance, good compressive strength, flexural strength, uniform color lasting, combining the performance of stone technology and cement-based wear-resistant material, so that the overall surface showed good shape, excellent mechanical properties, durability, simple construction, easy maintenance and long performance etc..
【技术实现步骤摘要】
水泥基彩砂耐磨材料
本专利技术属于地坪材料的制备领域，具体涉及一种水泥基彩砂耐磨材料。
技术介绍
耐磨地坪材料混凝土地面硬化剂，俗称金刚砂地坪，直接施工于即将初凝阶段的混凝土表面。地面硬化剂自上世纪70年代问世以来在欧美迅速普及，成为水磨石地面的完美换代产品，进入80年代末期，耐磨地坪更是发达国家的首选。矿物合金骨料（金刚砂）地面硬化剂由一定颗粒级配的矿物合金骨料，特种水泥，其它掺合料和外加剂组成，开袋即可使用。将其均匀地撒布在即将初凝阶段的混凝土表面，经专门手段加工，从而使其与混凝土地面形成一个整体，且具有高致密性和着色的高性能耐磨地面。
技术实现思路
本专利技术的目的在于针对现有技术的不足，提供一种水泥基彩砂耐磨材料。本专利技术的材料具有高强度、耐磨性好、抗压强度好、抗折强度好、颜色均匀持久，结合了磨石工艺和水泥基耐磨材料的性能，让整体的地面呈现良好的美观度、机械性能优异、耐久性长久、施工简便、易维护等性能。为实现上述目的，本专利技术采用如下技术方案：一种水泥基彩砂耐磨材料，由以下重量份的原料组成：硅酸盐水泥40-45份、彩砂60-65份、聚羧酸盐3-4份、硅酸钠...
【技术保护点】
一种水泥基彩砂耐磨材料，其特征在于：由以下重量份的原料组成：硅酸盐水泥40‑45份、彩砂60‑65份、聚羧酸盐3‑4份、硅酸钠2‑3份、颜料2‑4份、硅灰1‑1.5份、聚乙烯‑醋酸乙烯酯共聚物1‑2份、聚乙烯醇1‑2份。
【技术特征摘要】
1.一种水泥基彩砂耐磨材料，其特征在于：由以下重量份的原料组成：硅酸盐水泥40-45份、彩砂60-65份、聚羧酸盐3-4份、硅酸钠2-3份、颜料2-4份、硅灰1-1.5份、聚乙烯-醋酸乙烯酯共聚物1-2份、聚乙烯醇1-2份。2.根据权利要求1所述的水泥基彩砂耐磨材料，其特征在于：由以下重量份的原料组成：硅酸...
【专利技术属性】
技术研发人员：陈遵厚，陈亮，陈军军，谢桂秀，
申请(专利权)人：福州皇家地坪有限公司，
类型：发明
国别省市：福建,35