A method for preparing a titanium dioxide nanorods disclosed by the invention, first add four isopropyl titanate and strong electrolyte salt to 20% ammonia, in the rapid hydrolysis of four isopropyl titanate and intense mixing the mixture evenly, suspending liquid; then the reaction suspension into the rubber lining of stainless steel pressure still, prepared precipitate; finally the precipitated product with deionized water and dilute hydrochloric acid to prepare washing liquid for washing and drying continues, the titanium dioxide nanorods; the invention is prepared by one step hydrothermal TiO2 nanorods, and the morphology of flower like TiO2 nanorods for a plurality of aggregation, the nanorod diameter of 20nm ~ 50nm, the length of 500nm ~ 2500nm, the purity was more than 99%, the preparation method of the invention, the process is simple, controllable, has extensively. Usability.
【技术实现步骤摘要】
一种二氧化钛纳米棒的制备方法
本专利技术属于钛纳米材料制备工艺
，涉及一种二氧化钛纳米棒的制备方法。
技术介绍
纳米二氧化钛(TiO2)因具有化学稳定性好、抗光腐蚀、安全无毒、无二次污染及光催化能力强等优点，被广泛用于空气净化和污水处理等环境领域。研究表明，TiO2催化剂的性能与TiO2的晶型、晶粒大小和形貌有关，纳米二氧化钛棒因具有特殊的晶型结构和独特的一维形貌，导致其具有更为卓越的光电化学性能、光催化性能及机械力学性能，可用于光催化降解污染物，染料敏化太阳能电池和气敏元件等领域。然而，由于形成板钛矿(晶)型的二氧化钛的条件非常苛刻，故其在自然界中分布较少，人工制备纯相板钛矿(晶)型的纳米二氧化钛亦非常困难，不仅是制备步骤繁琐，而且是制得的产品纯度不高，常伴生有其他晶型的二氧化钛出现。
技术实现思路
本专利技术的目的是提供一种二氧化钛纳米棒的制备方法，解决了现有制备二氧化钛纳米棒的工艺步骤繁琐且制备的产品纯度不高的问题。本专利技术所采用的技术方案是，一种二氧化钛纳米棒的制备方法，具体按照以下步骤实施：步骤1、将四异丙基钛酸酯和强电解质无机盐添加至20％的氨水中...
【技术保护点】
一种二氧化钛纳米棒的制备方法，其特征在于，具体按照以下步骤实施：步骤1、将四异丙基钛酸酯和强电解质无机盐添加至20％的氨水中，在四异丙基钛酸酯快速水解的同时剧烈搅拌使其混合均匀，得悬浮液；步骤2、将步骤1制得的悬浮液放入橡胶衬里的不锈钢高压釜中进行反应，制得沉淀产物；步骤3、将步骤2制得的沉淀产物用去离子水及稀盐酸制得洗涤液进行洗涤，继续干燥，得到二氧化钛纳米棒。
【技术特征摘要】
1.一种二氧化钛纳米棒的制备方法，其特征在于，具体按照以下步骤实施：步骤1、将四异丙基钛酸酯和强电解质无机盐添加至20％的氨水中，在四异丙基钛酸酯快速水解的同时剧烈搅拌使其混合均匀，得悬浮液；步骤2、将步骤1制得的悬浮液放入橡胶衬里的不锈钢高压釜中进行反应，制得沉淀产物；步骤3、将步骤2制得的沉淀产物用去离子水及稀盐酸制得洗涤液进行洗涤，继续干燥，得到二氧化钛纳米棒。2.如权利要求1所述的一种二氧化钛纳米棒的制备方法，其特征在于，所述步骤1中的四异丙基钛酸酯与强电解质无机盐的质量比为1：4～6。3.如权利要求1或2所述的一种二氧化钛纳米棒的制备方法，其特征在于，强电解质...
【专利技术属性】
技术研发人员：高鹏涛，王荣生，周辉良，刘靖，
申请(专利权)人：宝鸡市永盛泰钛业有限公司，
类型：发明
国别省市：陕西,61