The invention discloses a modified flame retardant OSB, which comprises the following raw materials: nano silica mass fraction of 1 5%; nitrogen phosphorus flame retardant 10 wood shavings 43 30%; 79.5%; 2.5 adhesive agent 0.5 22%; 3%; the invention also discloses a preparation method of a modified the flame retardant of OSB; compared with the two commonly used methods, the invention adds silica modified flame retardant agents and additives in a molding process of OSB, better flame retardant effect of OSB in the preparation, fire resistance and higher stability. The preparation of flame retardant oriented strand board by using the preparation method of the invention can only be realized by adding simple spraying equipment in the sizing process, the equipment transformation cost is low, the two processing equipment is avoided, and the cost is saved.
【技术实现步骤摘要】
一种改性的阻燃定向刨花板及其制备方法
本专利技术属于木材科学与
，具体涉及一种改性的阻燃定向刨花板及其制备方法。
技术介绍
随着全球气候变暖的问题日益凸显，极端恶劣气候频发，以“低排放、低污染、低能耗”为主题的低碳经济越来越被人们认可和推崇。在这样的背景条件下，木业利用其与生俱来的“绿色”、“环保”、“清洁”的特性，在发展低碳经济、应对气候变化中，正发挥着日益重要的作用。木材及木制品有很好的固碳效果。只要不腐烂、不燃烧，木材及木制品的固碳功能就会长期、稳定的持续下去。有些固碳时间可达几十年、几百年。因此，增加木材使用，并尽量延长木材及木制品的使用寿命，对降低能耗、增加减排具有重要意义。据测算，森林每生产1吨木材，平均可固定二氧化碳1470kg，释放氧气1070kg。木材是四大建筑材料中唯一可再生的天然资源。世界森林持续减少，据联合国粮农组织对世界森林资源统计，2010年世界森林面积约为40亿hm2，而1990年的评估结果约40.8亿hm2。从年变化看，1990～2010年世界森林面积总计每年约减少400万hm2。保护天然林，培育人工速生林，是维护生态平衡最好...
【技术保护点】
一种改性的阻燃定向刨花板，其特征在于，包括如下质量百分比的原料：纳米二氧化硅1‑5％；阻燃剂10‑30％；木刨片43‑79.5％；胶黏剂2.5‑22％；助剂0.5‑3％。
【技术特征摘要】
1.一种改性的阻燃定向刨花板，其特征在于，包括如下质量百分比的原料：纳米二氧化硅1-5％；阻燃剂10-30％；木刨片43-79.5％；胶黏剂2.5-22％；助剂0.5-3％。2.根据权利要求1所述的阻燃定向刨花板，其特征在于，所述阻燃剂为磷酸铵、硼酸铵、硫酸铵、磷酸铵和聚磷酸铵中的一种或多种。3.根据权利要求1所述的阻燃定向刨花板，其特征在于，所述胶黏剂为异氰酸酯胶黏剂、酚醛树脂胶黏剂、三聚氰胺改性脲醛树脂胶和脲醛树脂胶中的一种或多种。4.根据权利要求1所述的阻燃定向刨花板，其特征在于，所述助剂为石蜡、氯化铵固化剂或甲醛消纳剂。5.一种如权利要求1-4任一所述改性的阻燃定向刨花板的制备方法，其特征在于，包括如下步骤：1)将干燥后的木刨片进行筛分；2)阻燃剂和纳米二氧化硅充分混合，得二氧化硅改性阻燃剂；3)将所述二氧化硅改性阻燃剂均匀喷涂到筛分后的木刨片上，得含有改性阻燃剂的木刨片；4)将胶黏剂和助剂分别均匀喷涂到含有改性...
【专利技术属性】
技术研发人员：李建立，张方文，李银凤，
申请(专利权)人：天津北新木业有限公司，
类型：发明
国别省市：天津,12
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。