The invention discloses a method for preparing a copper hydroxide, phosphomolybdic acid supported copper comprises the following steps: mixing water by adding 100 ~ 200mL to 4 ~ 5g, at the same time to the copper, slowly dropping 3 ~ phosphomolybdic acid 20 ~ 10g/L 100mL, dropping after aging at room temperature 24 ~ 48h, then remove supernatant, distilled water and washing the solid 3 ~ 4 times, 105 drying, a copper hydroxide load phosphomolybdic acid is obtained. The advantages of the invention are: the use of cupric hydroxide gradually dissolved in acidic conditions, phosphomolybdic acid precipitation of copper hydroxide formed on the surface can be obtained, phosphomolybdic acid supported copper catalyst uniform, using special structure of phosphomolybdic acid copper, efficient and rapid degradation of pollutants in water.
【技术实现步骤摘要】
一种氢氧化铜负载磷钼酸铜的制备方法
本专利技术涉及环境污染控制新材料领域，尤其涉及一种氢氧化铜负载磷钼酸铜的制备方法。
技术介绍
随着科技的发展，来自工农业生产中产生的毒害有机污染物严重威胁着环境和人类的健康，寻求一种新型高效的环境治理技术具有重要的意义。光催化技术因其节能、高效、污染物降解彻底、无二次污染优点，目前已成为一种具有重要应用前景的新兴环境治理技术。近年来，新型高效的可见光光催化剂的研制成为光催化技术中的一个重要研究内容，其中具有表面等离子共振效应的光催化材料，因其独特的表面物理化学性质和高效的可见光光催化性能，成为研究的热点之一。十二钼磷杂多酸的阴离子是一种1:12A型杂多酸阴离子，1826年首先由贝采利乌斯发现。这类1:12A型的结构首先由Keggin测得，因此常称为Keggin结构。其基本结构单元是四组三个钼氧八面体，每一组中三个钼氧八面体共用顶角上的氧原子，而磷原子位于四面体穴的中心。由于其特殊的结构，使得该物质有特别的性质。但磷钼酸铜至今未有相关报道。
技术实现思路
本专利技术的目的是为克服现有技术的不足，提供一种氢氧化铜负载磷钼酸铜的制备方法。本专利技术采用的技术方案是依次包括如下步骤：向100～200mL水中加入4～5g氢氧化铜，搅拌，同时向其中缓慢滴加3～10g/L的磷钼酸溶液20～100mL，滴加完成后，在室温下陈化24～48h，然后去除上清液，蒸馏水洗涤固体3～4次，105℃烘干，即得到一种氢氧化铜负载磷钼酸铜。本专利技术的优点是：利用氢氧化铜在酸性条件下逐步溶解，在氢氧化铜表面形成磷钼酸铜沉淀，即可获得负载均匀的磷钼酸铜催化剂...
【技术保护点】
一种氢氧化铜负载磷钼酸铜的制备方法，其特征是依次包括如下步骤：向100～200mL水中加入4～5g氢氧化铜，搅拌，同时向其中缓慢滴加3～10g/L的磷钼酸溶液20～100mL，滴加完成后，在室温下陈化24～48h，然后去除上清液，蒸馏水洗涤固体3～4次，105℃烘干，即得到一种氢氧化铜负载磷钼酸铜。
【技术特征摘要】
1.一种氢氧化铜负载磷钼酸铜的制备方法，其特征是依次包括如下步骤：向100～200mL水中加入4～5g氢氧化铜，搅拌，同时向其中缓慢滴加3～10g/L的...
【专利技术属性】
技术研发人员：宗玙，董平，黄文艳，蒋其民，薛小强，杨宏军，蒋必彪，
申请(专利权)人：常州大学，
类型：发明
国别省市：江苏,32