一种高分散性梭型氧化石墨烯及其制备方法技术
Highly dispersed shuttle type graphene oxide and preparation method thereof
The present invention discloses a kind of graphene oxide, whose morphology is shuttle type and / or ribbon. The invention also discloses the preparation method of the graphene oxide. Compared with the existing graphene oxide and graphene oxide of the invention has different morphology and structure; moreover, the invention of graphene oxide can reach above 10mg/mL solubility in water, is much larger than the existing graphene oxide solubility of 1 ~ 4mg/mL, can effectively avoid the graphene oxide in the application of the reunion and the piling phenomenon, greatly improving the convenience of application of graphene oxide; at the same time, the method, the preparation of graphene oxide is simple, safe, environmentally friendly, low energy consumption, less steps, simple operation, low cost, very suitable for the application of industry.
【技术实现步骤摘要】
一种高分散性梭型氧化石墨烯及其制备方法
本专利技术涉及一种高分散性梭型氧化石墨烯及其制备方法。
技术介绍
氧化石墨烯因其独特的二维结构和优异性能，近年来已成为国内外研究的热点，得到了越来越广泛的应用；应用时，是将氧化石墨烯分散或溶解于溶剂(通常为水)中，然后与其他原料混合均匀。然而，现有的氧化石墨烯在水中的溶解度很小，通常只有1～4mg/mL，应用时很容易发生团聚和堆砌，产生较大的结块，从而难以与其他原料混合均匀，存在加工性能差的缺陷，严重制约着它在很多方面的应用(参见：杨旭宇等.氧化石墨烯与石墨烯在溶剂中的分散性能研究.炭素技术.2014年，第3期，第33卷.)。为了克服现有技术的缺陷，同时，也为了获得一种在水中溶解度高的氧化石墨烯新产品，需要对现有的氧化石墨烯产品作进一步改进。
技术实现思路
本专利技术的目的在于提供一种氧化石墨烯，它具有高分散性、高溶解度、梭型形貌的特性。本专利技术提供的一种氧化石墨烯，其形貌为梭型和/或带状。进一步的，所述氧化石墨烯具有沿长轴的纵向裂缝。进一步的，所述氧化石墨烯中的羧基含量为5.4×10-3～7.8×10-3mol/g。进一步的...
【技术保护点】
一种氧化石墨烯，其特征在于：所述氧化石墨烯的形貌为梭型和/或带状。
【技术特征摘要】
1.一种氧化石墨烯，其特征在于：所述氧化石墨烯的形貌为梭型和/或带状。2.根据权利要求1所述的氧化石墨烯，其特征在于：所述氧化石墨烯具有沿长轴的纵向裂缝。3.根据权利要求1所述的氧化石墨烯，其特征在于：所述氧化石墨烯中的羧基含量为5.4×10-3～7.8×10-3mol/g。4.根据权利要求1所述的氧化石墨烯，其特征在于：所述氧化石墨烯的单位质量表面电荷为-521～-751C/g。5.根据权利要求1所述的氧化石墨烯，其特征在于：所述的氧化石墨烯在3440cm-1、2069cm-1、1637cm-1、1387cm-1、624cm-1和557cm-1处有红外吸收峰。6.根据权利要求1所述的氧化石墨烯，其特征在于：所述的氧化石墨烯在192nm、225nm、260nm和295nm处有紫外吸收峰。7....
【专利技术属性】
技术研发人员：杨中柱，蒋城，何巧，伍权，
申请(专利权)人：成都中医药大学，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。