一种氧化亚铜/氧化铜纳米复合物的室温固相制备方法技术
Preparation of cuprous oxide / Copper Oxide Nanocomposite at room temperature by solid phase method
The present invention relates to a method for preparing nano scale cuprous oxide / copper oxide composite by solid state reaction at room temperature. The nano cuprous oxide / copper oxide composite and pure phase cuprous oxide can be prepared by mixing the monovalent copper salt with the alkali at different ratios and by solid state chemical reaction at room temperature. The product was 20 granular material 50nm, are used in catalytic oxidation of carbon monoxide, showed good catalytic activity. The method has the advantages of simple operation, mild condition, environmental protection, no pollution, low cost of raw materials and easy production in large quantities. Cuprous oxide based nanomaterials are expected to play an important role in catalysis, energy storage, environmental monitoring and remediation.
【技术实现步骤摘要】
一种氧化亚铜/氧化铜纳米复合物的室温固相制备方法
本专利技术涉及纳米级氧化亚铜/氧化铜复合物的制备，属于复合材料合成与多相催化领域。
技术介绍
氧化亚铜(Cu2O)作为一种p型半导体材料,其禁带宽度只有2.0eV，在多个领域中展现出重要应用。具有纳米尺度的Cu2O拥有特殊的光学、电学、催化性质,在太阳能电池、传感器、污染物消除等方面有着潜在的应用。尤其是将Cu2O与其他氧化物复合，制得纳米复合物，其可展现出具有结构依赖性的性能特征。目前，用于制备氧化亚铜基纳米材料的方法主要有电化学法、多元醇法、水热法、沉淀法等。虽然具有不同尺寸、形貌的含Cu2O纳米复合物可由这些方法制备得到，但在合成过程中，需要消耗大量溶剂，且步骤繁琐、操作复杂。因此，开发一种绿色、简便的纳米Cu2O、含Cu2O复合物的合成方法尤为重要。
技术实现思路
本专利技术旨在提供一种纳米级氧化亚铜/氧化铜（Cu2O/CuO）复合物的制备方法。该方法通过在室温下，使原料经固相化学反应，一步得到Cu2O/CuO纳米复合物。本专利技术Cu2O/CuO纳米复合物的制备方法包括以下步骤：在室温下，将一价铜盐与碱按照摩...
【技术保护点】
一种氧化亚铜/氧化铜纳米复合物的室温固相制备方法，其包括以下步骤：在室温下，将一价铜盐与碱按照摩尔比为1:0.5~20混合，对混合物进行研磨或球磨10~120分钟，所得产物分别用氨水、水、乙醇洗涤，干燥后得到氧化亚铜/氧化铜纳米复合物。
【技术特征摘要】
1.一种氧化亚铜/氧化铜纳米复合物的室温固相制备方法，其包括以下步骤：在室温下，将一价铜盐与碱按照摩尔比为1:0.5~20混合，对混合物进行研磨或球磨10~120分钟，所得产物分别用氨水、水、乙醇洗涤，干燥后得到氧化亚铜/氧化铜纳米复合物。2.根据权利要求1所述的一种氧化亚铜/氧化铜纳米复合物的室温固相制备...
【专利技术属性】
技术研发人员：李怡招，谢月洪，刘保林，曹亚丽，贾殿赠，
申请(专利权)人：新疆大学，
类型：发明
国别省市：新疆,65