一种高灵敏度稀土掺杂钨青铜荧光探温材料制造技术
A high sensitivity rare earth doped tungsten bronze phosphor for exploring temperature
The invention discloses a high sensitive fluorescence probe temperature of rare earth doped tungsten bronze material and its preparation method, chemical formula of the rare earth doped tungsten bronze material for Ba4Gd0.65 xEr0.02YbxNb10O30, wherein, x = 0, 0.02, 0.05, 0.1. The invention adopts the high temperature solid phase reaction were prepared by the conventional Ba4Gd0.65 xEr0.02YbxNb10O30 material, simple process, low cost, good repeatability, convenient batch production. With the previous conversion temperature probe Ba4Gd0.65 xEr0.02YbxNb10O30 material than the material of the invention is a high sensitive fluorescence intensity ratio type temperature probe material, the maximum temperature detecting sensitivity of 573K to 0.013K
【技术实现步骤摘要】
一种高灵敏度稀土掺杂钨青铜荧光探温材料
本专利技术涉及上转换荧光探温材料领域，具体涉及一种高灵敏度稀土掺杂钨青铜荧光探温材料及其制备方法。
技术介绍
由于在环境科学、电子工业、生物医学、农业生产等重要领域的广泛应用，高灵敏度荧光探温材料的设计与开发是当前科研工作者关注的重要领域之一。近年来，稀土掺杂上转换发光材料由于在温度传感领域的广阔应用前景而得到人们特别关注。目前，许多稀土掺杂荧光强度比型无机材料的探温性能被研究报道，如在近红外980nm激发下Er与Yb共掺杂α-NaYF4，β-NaLuF4，Y2O3，Al2O3，Na0.5Bi0.5TiO3，Sr2Bi4Ti5O18，Bi4Ti3O12，Bi7Ti4NbO21的最大探温灵敏度分别为0.0030K-1，0.0052K-1，0.0044K-1，0.0051K-1，0.0035K-1，0.0042K-1，0.0043K-1，0.0044K-1。然而，以上材料的探温灵敏度还较低，这不利于材料实际应用。最近研究表明，由于具有相对较低的声子能量与稳定的物理化学特性，钨青铜材料是一种很有前景的上转换发光基质材料，其在探温领...
【技术保护点】
一种高灵敏度稀土掺杂钨青铜上转换荧光强度比型探温材料，该材料的化学式为Ba4Gd0.65‑xEr0.02YbxNb10O30，其中，x＝0，0.02，0.05，0.1。
【技术特征摘要】
1.一种高灵敏度稀土掺杂钨青铜上转换荧光强度比型探温材料，该材料的化学式为Ba4Gd0.65-xEr0.02YbxNb10O30，其中，x＝0，0.02，0.05，0.1。2.如权利要求1所述探温材料的制备方法，其特征为：以BaCO3、Gd2O3、Er2O3、Yb2O3、Nb2O5原料，按照化学计量比准确称取所需原料后将之混合，利用酒精为溶剂在行星式球磨机中研磨24h，之后将混合均匀的粉末进行干燥，于1300℃下预烧8小时。将烧结的粉末重新研磨后在1350℃下煅烧5小时，然后用玛瑙研钵研磨得上转换荧光粉。3.如权利要求1所述材料探温应用，其特征为：在980nm近红外激光激发下，材料展现明亮的...
【专利技术属性】
技术研发人员：魏通，谢一帆，董泽，
申请(专利权)人：中国民航大学，
类型：发明
国别省市：天津,12