The present invention discloses a kind of adhesive for food packaging, according to the quality of the copies, consists of the following components: polyester diol 50~55 parts, ethyl acetate 65~70, phthalic anhydride, two 2~3 epoxy resin 12~15, isophorone diisocyanate trimer 10~12 two, phosphate 0.1~0.2. The preparation method comprises the following steps: step one: the formula amount of polyester glycol, ethyl acetate, phthalic anhydride, two phosphoric acid, epoxy resin in a reaction kettle, heating up to 60 DEG C, the stirrer, the stirring 4H; step two: isophorone isocyanate trimer with two mixture to stir in after stirring, cooling to room temperature, the adhesive used for food packaging. The adhesive for food packaging prepared by the invention has good water resistance, high solid content in the adhesive and fast drying speed during the bonding process.
【技术实现步骤摘要】
一种食品包装用胶黏剂及其制备方法
本专利技术涉及一种食品包装用胶黏剂及其制备方法，应用于胶黏剂加工
技术介绍
胶黏剂是现代工业发展和人类生活水平提高必不可少的重要材料，在现代经济、国防及现代科技中发挥着重大作用，在食品包装领域常用到水性聚氨酯胶，由于乳化剂的使用或分子中亲水性离子基团的引入，使水性聚氨酯胶耐水性降低，且市场上的水性聚氨酯胶固含量降低，干燥速度较慢。
技术实现思路
为解决上述的问题，本专利技术公开了一种食品包装用胶黏剂及其制备方法。本专利技术公布了一种食品包装用胶黏剂，按质量份数，由下列组分构成：聚酯二元醇50~55份、乙酸乙酯65~70份、邻苯二甲酸酐2~3份、环氧树脂12~15份、异佛尔酮二异氰酸三聚物10~12份、磷酸0.1~0.2份。上述环氧树脂为1002#环氧树脂。本专利技术的制备方法如下：步骤一：将配方量的聚酯二元醇、乙酸乙酯、邻苯二甲酸酐、磷酸、环氧树脂置于反应釜内，升温至60℃，开启搅拌器，搅拌4h；步骤二：将异佛尔酮二异氰酸三聚物加入至搅拌后的混合液中，搅拌均匀后，冷却至常温即得食品包装用胶黏剂。采用本技术方案，本专利技术的有...
【技术保护点】
一种食品包装用胶黏剂，其特征在于：按质量份数，由下列组分构成：聚酯二元醇50~55份、乙酸乙酯65~70份、邻苯二甲酸酐2~3份、环氧树脂12~15份、异佛尔酮二异氰酸三聚物10~12份、磷酸0.1~0.2份。
【技术特征摘要】
1.一种食品包装用胶黏剂，其特征在于：按质量份数，由下列组分构成：聚酯二元醇50~55份、乙酸乙酯65~70份、邻苯二甲酸酐2~3份、环氧树脂12~15份、异佛尔酮二异氰酸三聚物10~12份、磷酸0.1~0.2份。2.如权利要求1所制得的一种食品包装用胶黏剂，其特征在于，制备方法如下：步骤一：将配...
【专利技术属性】
技术研发人员：何金平，
申请(专利权)人：安徽友捷包装材料有限公司，
类型：发明
国别省市：安徽,34