一种超级电容器的石墨烯膜电极材料的制备方法技术

本发明专利技术提供了一种超级电容器的石墨烯膜电极材料的制备方法，将氧化石墨烯膜或者还原氧化石墨烯膜充分浸泡在盛有浓硫酸的聚四氟乙烯反应釜中，在120℃～180℃反应3～24小时，室温冷却、蒸馏水洗涤，干燥，制备得到石墨烯膜电极材料。以该膜为电极材料组装成的超级电容器具有较好的电容性能，特别是其具有超好的循环稳定性。本发明专利技术操作过程简便。所制备的产品可用于对称或者非对称超级电容器电极材料。

Preparation method of graphene film electrode material for supercapacitor

The present invention provides a method for preparing graphene film electrode material for super capacitor, the graphene oxide film or reduced graphene oxide film fully immersed in PTFE reactor filled with sulfuric acid, at 120 to 180 DEG C for 3~24 hours at room temperature, cooling the reaction, distilled water washing and drying. Preparation of graphene film electrode materials. The supercapacitor assembled with this film as electrode material has good capacitance performance, especially its excellent cycle stability. The operation process of the invention is simple. The prepared products can be used for symmetric or asymmetric supercapacitor electrode materials.

【技术实现步骤摘要】
一种超级电容器的石墨烯膜电极材料的制备方法
本专利技术涉及膜电极材料的制备，特别涉及一种可用于超级电容器的石墨烯膜电极材料的的制备方法。
技术介绍
超级电容器作为一种介于电池和传统电容器之间的新型储能装置，兼具电池能量密度高和传统电容功率密度大、结构简单等特点，在新型清洁能源等领域有潜在的应用价值。近年来消费电子产品正向着小型化、柔性可折叠的方向发展，激发了人们对可用于小型化电子设备的高体积性能超级电容器的研究兴趣，开发具有高功率密度和高能量密度的超级电容器满足体积和质量有限的电子器件最大程度地利用，已发展成储能设备研究的重要方向[D.Yu,K.Goh,H.Wang,L.Wei,W.Jiang,Q.Zhang,L.Dai,Y.Chen,Scalablesynthesisofhierarchicallystructuredcarbonnanotube-graphenefibresforcapacitiveenergystorage,Nat.Nanotechnol.2014,9,555-562]。在组成超级电容器的所有部件中，电极材料对超级电容器的性能有着至关重要的影响。石墨烯由于其具有本文档来自技高网...

【技术保护点】
一种超级电容器石墨烯膜电极材料的制备方法，其特征在于，包括如下步骤：将氧化石墨烯膜或者还原氧化石墨烯膜充分浸泡在盛有浓硫酸的聚四氟乙烯反应釜中，在120℃～180℃反应3～24小时，室温冷却、蒸馏水洗涤，干燥，制备得到石墨烯膜电极材料。

【技术特征摘要】
1.一种超级电容器石墨烯膜电极材料的制备方法，其特征在于，包括如下步骤：将氧化石墨烯膜或者还原氧化石墨烯膜充分浸泡在盛有浓硫酸的聚四氟乙烯反应釜中，在120℃～180℃反应3～24小时，室温冷却、蒸馏水洗涤，干燥，制备得到石墨烯膜电极材料...