一种镀镍铜线制造技术

本发明专利技术公开了一种镀镍铜线，包括铜芯，其特征在于，所述铜芯的外侧包覆树脂涂层，所述树脂涂层的外侧包覆合金层，所述合金层的外侧包覆镀镍层，所述铜芯的直径为0.32‑0.47mm，所述树脂涂层的厚度为1.2‑1.8μm，所述合金层的厚度为2.8‑3.3μm，所述镀镍层的厚度为3.0‑4.5μm。经试验证明，本发明专利技术制得的无铅镀镍铜线具有良好的耐腐蚀性、耐热性；其伸长率为22.7‑23.6％、导电率低于0.011Ω·mm

A nickel plated copper wire

The invention discloses a nickel plated copper, including copper, which is characterized in that the outer side of the copper coated resin coating, the outer coating resin coated alloy layer, wherein the outer side of the alloy layer coated nickel plating layer, the copper core diameter of 0.32 0.47mm, the resin coating thickness 1.2 1.8 m, the alloy layer thickness of 2.8 3.3 mu m, the nickel plating layer with a thickness of 3 4.5 M. Experiments show that the lead-free nickel copper prepared by the invention has good corrosion resistance and heat resistance; the elongation rate is 22.7, 23.6% conductivity is less than 0.011. Mm.

【技术实现步骤摘要】
一种镀镍铜线
本专利技术涉及材料加工
，尤其涉及了一种镀镍铜线。
技术介绍
目前市场上常见的镀镍铜线为两层结构，即在铜芯的外围镀上一层金属镍，镍在空气中易钝化，具有良好的耐碱性，与盐酸和硫酸之间的作用也比较缓慢，因此铜芯外层的镀镍层可以起到良好的保护作用。镀镍铜线常被应用于电线电缆的导电线芯，但是由于镍层的耐高温效果差，当铜芯温度过高会导致镀镍层出现点状漏洞的现象，影响了产品的质量。中国专利，专利名称：一种镀镍软圆铜线，申请公布号：CN104064248A，公开的镀镍铜线，其结构从内到外依次为铜线层、镀镍层、镀镍层和外护层，其外护层为添加了15-20％的活性煅烧超细高岭土的聚氯乙烯阻燃材料，提高了产品的耐腐蚀性和耐高温能力，但其保护层的厚度大于镀镍层或镀镍层的厚度，会导致镀镍铜线的导电性及力学性能受到影响。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种镀镍铜线，具备优良力学性能、耐热性和导电性。一种镀镍铜线，包括铜芯，所述铜芯的外侧包覆树脂涂层，所述树脂涂层的外侧包覆合金层，所述合金层的外侧包覆镀镍层，所述铜芯的直径为0.32-0.47mm，所述树脂涂层的厚度为1本文档来自技高网...

【技术保护点】
一种镀镍铜线，包括铜芯，其特征在于，所述铜芯的外侧包覆树脂涂层，所述树脂涂层的外侧包覆合金层，所述合金层的外侧包覆镀镍层，所述铜芯的直径为0.32‑0.47mm，所述树脂涂层的厚度为1.2‑1.8μm，所述合金层的厚度为2.8‑3.3μm，所述镀镍层的厚度为3.0‑4.5μm。

【技术特征摘要】
1.一种镀镍铜线，包括铜芯，其特征在于，所述铜芯的外侧包覆树脂涂层，所述树脂涂层的外侧包覆合金层，所述合金层的外侧包覆镀镍层，所述铜芯的直径为0.32-0.47mm，所述树脂涂层的厚度为1.2-1.8μm，所述合金层的厚度为2.8-3.3μm，所述镀镍层的厚度为3.0-4.5μm。2.根据权利要求1所述的一种镀镍铜线，其特征在于，所述树脂涂层包括按照重量份计的如下组份：环氧树脂35-45份、有机硅树脂15-20份、填料5-12份、增稠剂1-3份、成膜助剂1.5-2.5份。...

【专利技术属性】
技术研发人员：王彬，徐金龙，刘大亮，
申请(专利权)人：赣州西维尔金属材料科技有限公司，
类型：发明
国别省市：江西,36