The invention relates to the technical field of solar cell, especially a crystal silicon solar cell without the main gate is silver paste, its composition comprises the following raw materials in weight percent: 75 to 90% silver, glass powder is 1 ~ 8%, 5 ~ 15% organic carrier, agent 0 ~ 3%, solvent, organic carrier used ethyl cellulose, one or more other resins from rosin, polyamide, polyester, acrylic resin, alkyd resin, epoxy resin. The silver paste is made of ethyl cellulose grease, which improves the printing quality of the slurry without the main grid screen, and ensures the high aspect ratio of printing.
【技术实现步骤摘要】
晶体硅太阳能电池无主栅银浆料及其制备方法
本专利技术涉及太阳能电池
，尤其是一种晶体硅太阳能电池无主栅银浆料及其制备方法。
技术介绍
现阶段，太阳能光伏行业逐渐摆脱了往昔的阴霾，在国家政策的大力支持下，终于迎来了黄金发展期，与此同时，越来越激烈的行业竞争也加速了光伏行业的产业整合，随着光伏企业逐渐走出去的步伐加快，国际贸易也是争端不止，光伏“双反”步步紧逼之下，一定程度上促进光伏企业研发更高效的光伏产品。无主栅印刷方式在这种竞争激烈的大环境下应运而生，电池正面仅印刷细栅，无主栅电池的优势在于通过减少遮光面积和电阻损失增加组件效率，减少25%遮光面积，通过使用铜线代替银主栅降低成本，银浆损耗减少50%左右，传统的技术往往在提高效率的同时增加了成本，但无主栅技术即降低了成本又提高了效率，现有无主栅技术在电池印刷过程中不够流畅，印刷质量满足不了人们日益增长的使用需求。
技术实现思路
为了克服现有的无主栅技术印刷不够流畅的不足，本专利技术提供了一种晶体硅太阳能电池无主栅银浆料，通过在正银浆料中采用乙基纤维素制作有机载体来解决问题。本专利技术解决其技术问题所采用的技术方案...
【技术保护点】
一种晶体硅太阳能电池无主栅银浆料，其特征是，由下列重量百分比的原料组成：银粉75～90%，玻璃粉1～8%，有机载体5～15%，助剂0～3%，余量为溶剂。
【技术特征摘要】
1.一种晶体硅太阳能电池无主栅银浆料，其特征是，由下列重量百分比的原料组成：银粉75～90%，玻璃粉1～8%，有机载体5～15%，助剂0～3%，余量为溶剂。2.根据权利要求1所述的晶体硅太阳能电池无主栅银浆料，其特征是，所述有机载体为一种或几种有机树脂与不同挥发速度的有机溶剂组成。3.根据权利要求2所述的晶体硅太阳能电池无主栅银浆料，其特征是，所述有机树脂占有机载体质量百分比的10%～40%。4.根据权利要求2所述的晶体硅太阳能电池无主栅银浆料，其特征是，所述有机树脂为乙基纤维素及其它树脂。5.根据权利要求4所述的晶体硅太阳能电池无主栅银浆料，其特征是，所述乙基纤维素选自N系列和T系列的一种或几种，其它树脂选自松香、聚酰胺、聚酯、丙烯酸树脂、醇酸树脂、环氧树脂中的一种或多种。6.根据权利要求1所述的晶体硅太阳能电池无主栅银浆料，其特征是，所述有机溶剂占有机载体质量百分比的40～90%。7.根据权利要求6所述的晶体硅太阳能电池无主栅银浆料，其特征是，所述有机溶剂选自丁基卡必醇、丁基卡必醇醋酸酯、松油醇、乙二醇丁醚、乙二醇苯醚、...
【专利技术属性】
技术研发人员：任中伟，赵德平，丁兴隆，
申请(专利权)人：北京市合众创能光电技术有限公司，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。