一种复合变质过共晶铝硅合金及其制备方法技术
Composite modified hypereutectic Al Si alloy and preparation method thereof
The invention discloses a composite modified aluminum silicon alloy and preparation method of eutectic, in weight percentage: 17% to 23% silicon components; rare earth 0.2% ~ 1%; aluminum titanium boron intermediate alloy from 0.1% to 0.8%; the other is aluminum. The aluminium and silicon after mixing at 790 to 820 DEG C temperature heating to melt after heat 6 ~ 12min, at 730 to 750 DEG C temperature of 15 ~ 20min, C2Cl6 melt; aluminum foil coating is pressed into the melt mixing, refining, slag and gas, slag forming from 700 to 710 DEG C for casting, hypereutectic Al Si alloy; melting after adding rare earth and Al-Ti-B intermediate alloy compound modification of hypereutectic Al Si alloy. The beneficial effect of the invention is that the preparation method is simple and easy to operate, and the composite modification effect is stable.
【技术实现步骤摘要】
一种复合变质过共晶铝硅合金及其制备方法
本专利技术属于过共晶铝硅合金的变质
，涉及一种复合变质的过共晶铝硅合金及其制备方法。
技术介绍
亚共晶Al-Si合金和过共晶Al-Si合金都被广泛的应用于汽车发动机、活塞、缸体、缸盖等零部件的生产。相比于亚共晶Al-Si合金，过共晶Al-Si合金因其良好的耐磨、耐蚀性和良好的高温性能被广泛地应用。但不足的是，过共晶Al-Si合金组织中存在粗大不规则的初生Si及针片状的共晶Si，它们割裂了合金基体的连续性，使得合金的力学性能大大降低。因此，变质过共晶铝硅合金中的Si相，获得细小均匀分布的组织，对提高过共晶Al-Si合金的性能和扩大使用范围至关重要。目前，过共晶铝硅合金的变质方法主要有单一变质和复合变质两种方式。其中，单一变质已得到了许多实验的证实，如P盐可以有效的变质初生Si，而Sr盐及Na盐对共晶Si的变质效果良好。可是，当两种不同变质剂混合使用，进行复合变质时，反而由于变质剂之间的化学反应使过共晶Al-Si合金的变质效果减弱，丧失原有的变质能力，不能起到细化和变质Si相的作用。Al-5Ti-B作为一种良好的细化剂，已...
【技术保护点】
一种复合变质过共晶铝硅合金，其特征在于：包括以下按质量百分比计组分：硅 17％～23％；稀土 0.2％～1.0％；铝钛硼中间合金 0.1％～0.8％；余量为铝。
【技术特征摘要】
1.一种复合变质过共晶铝硅合金，其特征在于：包括以下按质量百分比计组分：硅17％～23％；稀土0.2％～1.0％；铝钛硼中间合金0.1％～0.8％；余量为铝。2.按照权利要求1所述一种复合变质过共晶铝硅合金，其特征在于：所述稀土为镱；所述铝钛硼中间合金为Al-5Ti-1B。3.按照权利要求1所述一种复合变质过共晶铝硅合金，其特征在于：所述稀土和铝钛硼中间合金的质量比为5:1、5:2、5:3、5:4、5:5。4.按照权利要求1所述一种复合变质过共晶铝硅合金的制备方法，其特征在于按照以下步骤进行：(1)将铝、结晶硅混合后，在790℃～820℃温度下加热至全部熔化后保温6～12min，在73...
【专利技术属性】
技术研发人员：李庆林，住玉乾，李进宝，李斌强，张建斌，
申请(专利权)人：兰州理工大学，
类型：发明
国别省市：甘肃,62
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。