The invention provides a high temperature resistant and corrosion resistant test tube rack, which is characterized in that the weight includes the following components: high temperature nylon: 35~45; rare earth oxides: 6~12; polyphenylene ether grafted maleic anhydride: 13~18; 2~6: polyethylene wax; zinc stearate: 5~11; inorganic filler: 2~7 0.5~4; heat stabilizer; toughening agent 1~5; antioxidant: 0.5~3. A kind of high temperature resistant and corrosion resistant test tube rack of the invention, has excellent resistance to high temperature and acid, alkali, organic solution corrosion resistance, after use in a long time, it will not lead to deformation, corrosion and damage of the test tube rack, the use of safety and stability, prolong the service life of tube frame.
【技术实现步骤摘要】
一种耐高温耐腐蚀试管架
本专利技术涉及一种耐高温耐腐蚀试管架。
技术介绍
在日常的实验室或工业生产中，经常需要在化学反应、生物反应等过程使用试管。试管架是用于放置试管的一种实验器材。由于试管在使用时经常需要进行加热，处于高温的试管放置于试管架时，容易使得试管架发生变形，使用时间久后导致试管架不稳，影响使用，此外，试管壁残留的酸、碱液或者有机溶液，对试管架会造成腐蚀，影响试管架的美观及使用。因此，需要一种耐高温的试管架。
技术实现思路
为解决上述存在的问题，本专利技术的目的在于提供一种耐高温耐腐蚀试管架。所述耐高温耐腐蚀试管架，具有优异的耐高温及耐酸、碱、有机溶液腐蚀性能，在长时间使用后，也不会导致试管架的变形、腐蚀及损坏，使用安全稳定，延长试管架的使用寿命。为达到上述目的，本专利技术的技术方案是：一种耐高温耐腐蚀试管架，包括如下重量份数的组分：高温尼龙：35~45份；稀土氧化物：6~12份；聚苯醚接枝马来酸酐：13~18份；聚乙烯蜡：2~6份；硬脂酸锌：5~11份；无机填料：2~7份；热稳定剂：0.5~4份；增韧剂：1~5份；抗氧化剂：0.5~3份。进一步地，包括如下...
【技术保护点】
一种耐高温耐腐蚀试管架，其特征在于，包括如下重量份数的组分：高温尼龙：35~45份；稀土氧化物：6~12份；聚苯醚接枝马来酸酐：13~18份；聚乙烯蜡：2~6份；硬脂酸锌：5~11份；无机填料：2~7份；热稳定剂：0.5~4份；增韧剂：1~5份；抗氧化剂：0.5~3份。
【技术特征摘要】
1.一种耐高温耐腐蚀试管架，其特征在于，包括如下重量份数的组分：高温尼龙：35~45份；稀土氧化物：6~12份；聚苯醚接枝马来酸酐：13~18份；聚乙烯蜡：2~6份；硬脂酸锌：5~11份；无机填料：2~7份；热稳定剂：0.5~4份；增韧剂：1~5份；抗氧化剂：0.5~3份。2.根据权利要求1所述的耐高温耐腐蚀试管架，其特征在于，包括如下重量份数的组分：高温尼龙：35~40份；稀土氧化物：8~12份；聚苯醚接枝马来酸酐：13~15份；聚乙烯蜡：2~4份；硬脂酸锌：5~7份；无机填料：3~7份；热稳定剂：0.5~2份；增韧剂：1~3份；抗氧化剂：0.5~2份。3.根据权利要求1所述的耐高温耐腐蚀试管架...
【专利技术属性】
技术研发人员：陆裕聪，
申请(专利权)人：苏州坤阳机械科技有限公司，
类型：发明
国别省市：江苏,32