The invention discloses a shear wall plaster mortar, the mortar material consists of Portland cement 60~80, modified palm fiber 40~50 parts, quartz sand, glass beads 34~38 20~30, fly ash 20~30, aluminum sulfate 0.1~0.5 and water 50~100; the preparation method of the modified of palm silk: palm silk drying to a moisture content of less than 5wt%, the palm thread is placed in the water bath dry ratio of six methyl phosphoryl 1:12 three amine solution, water bath is heated to 80 DEG C, after 1.5~3 hours of treatment, remove the palm silk, washing and drying. The present invention utilizes six methyl three phosphoryl amine solution of palm fiber was modified for the first time, in order to improve the performance of soft palm silk, and will be changed after the palm fiber added to the mortar, the elastic modulus of the mortar is reduced, so that the invention of mortar has high compressive strength, wear resistance, shock resistance and crack resistance excellent characteristics.
【技术实现步骤摘要】
一种抗震墙粉刷用砂浆
本专利技术涉及建筑材料领域，具体涉及一种抗震墙粉刷用砂浆。
技术介绍
水泥砂浆又称灰浆，是用无机胶凝材料与细集料和水按比例拌合而成的建筑材料，多用于建筑施工中砌筑和抹灰工程，以实现建筑结构和表面防护、装饰。由于砂浆的强度远远低于砌块，在地震作用下，灰缝承载力不足成为引起砌体结构破坏的主要原因之一。现有砂浆的强度相对较低、材料脆性较大及变形能力较差，导致砌体结构在地震作用下承载力迅速下降，使其应用受到了大大的限制。可见，现有的砂浆具有易脆性、抗裂和抗震性能差的缺点，专利技术一种具有抗震性能的砂浆具有重要的意义。
技术实现思路
本专利技术的目的在于针对现有技术不足，提供一种抗震墙粉刷用砂浆。本专利技术首次利用六甲基磷酰三胺溶液对棕榈丝进行改性，以此来改善棕榈丝的柔软性能，并将改性后的棕榈丝添加到砂浆中，降低了砂浆的弹性模量，使得本专利技术砂浆具有抗压强度高、耐磨性、抗震性和抗裂性能优异等显著特点。为实现上述目的，本专利技术采用如下技术方案：一种抗震墙粉刷用砂浆，按重量份数计，所述砂浆的原料组成为：硅酸盐水泥60~80份、改性棕榈丝40~50份、石英砂...
【技术保护点】
一种抗震墙粉刷用砂浆，其特征在于：按重量份数计，所述砂浆的原料组成为：硅酸盐水泥60~80份、改性棕榈丝40~50份、石英砂34~38份、玻化微珠20~30份、粉煤灰20~30份、硫酸铝0.1~0.5份和水50~100份；所述改性棕榈丝的制备方法为：将棕榈丝干燥至含水量低于5wt%后，取干燥的棕榈丝置于水浴比为1:12的六甲基磷酰三胺溶液中，水浴升温至80℃，处理1.5~3小时后，取出棕榈丝，水洗并烘干。
【技术特征摘要】
1.一种抗震墙粉刷用砂浆，其特征在于：按重量份数计，所述砂浆的原料组成为：硅酸盐水泥60~80份、改性棕榈丝40~50份、石英砂34~38份、玻化微珠20~30份、粉煤灰20~30份、硫酸铝0.1~0.5份和水50~100份；所述改性棕榈丝的制备方法为：将棕榈丝干燥至含水量低于5wt%后，取干燥的棕榈丝置于水浴比为1:12的六...
【专利技术属性】
技术研发人员：李钻水，
申请(专利权)人：福建省永泰建筑工程公司，李钻水，
类型：发明
国别省市：福建,35