The present invention belongs to the field of preparation of binder, and relates to the preparation method of glass material for synthesizing low-temperature vitrified bond by sol gel method. Compared with the traditional preparation process, it has a lower heat treatment temperature and improves the toughness and strength of the material. A method for treating metal alkoxides or inorganic substances by solution, sol, gel, and then heat treatment to form oxides or other solid compounds. The method has the advantages of homogeneous composition, high purity, low heat treatment temperature, low production cost and controllable particle size. It is mainly used in the preparation of glass, coating, fiber, functional ceramic powder and so on.
【技术实现步骤摘要】
一种溶胶凝胶法合成低温陶瓷结合剂用玻璃料的制备方法
本专利技术属于结合剂的制备领域，涉及一种溶胶凝胶法合成超硬材料低温陶瓷结合剂用玻璃料的制备方法。陶瓷结合剂有很多优点，比如它的耐水性、耐油性、耐酸碱性；可以适应各种冷却液的作用；磨具刚性好，不易变形，工件精度高；磨具疏松多孔，易排屑，不容易发生堵塞和工件的烧伤破坏；自锐性好，容易修整且时间间隔长，加工效率高；其制备工艺决定了陶瓷结合剂在磨削高温前提下依然可以与金刚石发生良好的结合现象。当前，陶瓷结合剂金刚石磨具广泛应用在超硬磨料刀具等工具的粗磨削、精磨削和超精磨削以及宝石、陶瓷等硬脆原料的磨削和加工，特别是在对单晶金刚石的研磨方面，表现出了更加优异的特性，比如磨耗比小，成本低廉，加工效率高。鉴于陶瓷结合剂金刚石磨具的上述优点，可以明显看出陶瓷结合剂金刚石磨具在磨削加工应用中展现出的突出作用。陶瓷结合剂按照不一样的标准有差别的分类，按照热处理工艺中结合剂状态的差异，可以分为烧熔和烧结结合剂；按照制备流程和组成的差异，还可以分为三类：传统矿物、玻璃熔炼和微晶玻璃结合剂。无论是哪种分类，传统的制造方法大多为氧化物高...
【技术保护点】
本专利技术属于结合剂的制备领域，涉及一种溶胶凝胶法合成低温陶瓷结合剂用玻璃料的制备方法；所述的制备方法包括以下步骤：a、按比例称取摩尔比醋酸锌（Zn(Ac)2·2H2O)、硬脂酸锌或氯化锌30~35%，硼酸20~30%，正硅酸乙酯或四氯化硅50~60%，溶剂为无水乙醇和去离子水，催化剂为盐酸，络合剂为柠檬酸、草酸或硬脂酸10~30%，配置成相应的锌盐和硼酸的混合水溶液Ⅰ，硅盐的醇溶液Ⅱ，在Ⅱ中加入络合剂搅拌，将Ⅰ和Ⅱ缓慢滴定、常温搅拌、均匀混合后制备出相应的溶胶；b、在步骤a所制备的溶胶中加入盐酸，调pH值，混合搅拌，水浴保温后，放置陈化，制备出相应的湿凝胶；c、将步骤b所...
【技术特征摘要】
1.本发明属于结合剂的制备领域，涉及一种溶胶凝胶法合成低温陶瓷结合剂用玻璃料的制备方法；所述的制备方法包括以下步骤：a、按比例称取摩尔比醋酸锌（Zn(Ac)2·2H2O)、硬脂酸锌或氯化锌30~35%，硼酸20~30%，正硅酸乙酯或四氯化硅50~60%，溶剂为无水乙醇和去离子水，催化剂为盐酸，络合剂为柠檬酸、草酸或硬脂酸10~30%，配置成相应的锌盐和硼酸的混合水溶液Ⅰ，...
【专利技术属性】
技术研发人员：侯永改，周青海，马加加，李文凤，高元，李广峰，黄庆飞，丁志静，
申请(专利权)人：河南工业大学，
类型：发明
国别省市：河南,41