Air knife coating type sisal the invention relates to a radiation protection fabric, is on the outer surface of sisal fabric using air knife coating way to decorate a layer of functional coating, coating the coating slurry function relates to the preparation of the coating agent, silane, Zinc Oxide and crosslinking agent is added into pulping tank. After mixing evenly, with ammonia pH adjusted to 7.5 ~ 8.5, standing for 2 to 4 hours, and then using the method of air knife coating applied to the sisal fabric surface at 80 DEG C, under drying for 0.5 hours, from 120 to 135 DEG C curing environment 1 ~ 1.5 hours, finally in natural conditions to balance 8 hours. After the surface of sisal fabric is protected by coating material, the fabric has better radiation protection characteristics, and improves the quality of fabric.
【技术实现步骤摘要】
一种辐射保护的气刀涂布式剑麻织物面料
本专利技术属于剑麻织物面料
，具体涉及一种辐射保护的气刀涂布剑麻织物面料。
技术介绍
剑麻纤维质地坚韧，耐磨、耐盐碱、耐腐蚀，广泛运用在运输、渔业、石油、冶金等各种行业，具有重要的经济价值。世界剑麻进出口贸易在不断增长，而中国目前自产的剑麻纤维却不能满足国内的需要，并且随着剑麻纤维用途的不断增加，中国每年都在增加剑麻纤维的进口量。同时剑麻还有重要的药用价值，剑麻在面料上的应用也逐渐被市场所关注，不断开发剑麻织物面料的新功能是剑麻织物面料发展的趋势。
技术实现思路
本专利技术的目的是提供一种辐射保护的气刀涂布式剑麻织物面料。本专利技术解决上述问题所采用的技术方案为：一种辐射保护的气刀涂布式剑麻织物面料，是在剑麻基布的外表面采用气刀涂布的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、氧化锌和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至7.5～8.5范围，静置2～4小时，然后采用气刀涂布的方式施加到剑麻基布表面，于80℃环境下烘干0.5小时，于120～135℃环境下固化1～1.5小时，最后在自然条件下平...
【技术保护点】
一种辐射保护的气刀涂布式剑麻织物面料，其特征在于：是在剑麻基布的外表面采用气刀涂布的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、氧化锌和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至7.5～8.5范围，静置2～4小时，然后采用气刀涂布的方式施加到剑麻基布表面，于80℃环境下烘干0.5小时，于120～135℃环境下固化1～1.5小时，最后在自然条件下平衡8小时以上。
【技术特征摘要】
1.一种辐射保护的气刀涂布式剑麻织物面料，其特征在于：是在剑麻基布的外表面采用气刀涂布的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、氧化锌和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至7.5～8.5范围，静置2～4小时，然后采用气刀涂布的方式施加到剑麻基布表面，于80℃环境下烘干0.5小时，于12...