The present invention relates to PVC composition and its preparation method and application thereof, PVC composition mainly comprises the following components: PVC resin 100 weight portions; 30 to 1500 parts by weight of TPU, preferably 40 to 1200 parts by weight, preferably 50 to 900 parts by weight; the composition can be used for the preparation of refrigeration equipment seal, the compositions for the preparation of the seal seal compared with traditional PVC, has high mechanical properties, solvent resistance, resilience and resistance to migration.
【技术实现步骤摘要】
一种PVC组合物及其制备方法和用途
本专利技术涉及一种PVC组合物及其制备方法和用途，属于材料领域。
技术介绍
聚氯乙烯(PVC)具有良好的耐化学性、价格低廉、易加工和原料来源广泛的特点，被广泛应用于密封条领域。当前制冷器具(主要为冰箱和冰柜)用密封条大多数为软质PVC材料。对于PVC密封条，主要成分为PVC树脂，增塑剂，填料及一些其它助剂。增塑剂一般按功能进行复配组合，一般以苯二甲酸酯类低分子物如邻苯二甲酸二异壬酯(DINP)与对苯二甲酸二辛酯(DOTP)为主，添加一些耐寒增塑剂为辅，如对苯二甲酸二辛酯(DOA)、癸二酸二辛酯(DOS)等，添加具有稳定剂功能的环氧增塑剂。但环保问题一直是该体系的重要课题，邻苯二甲酸酯类增塑剂因对环境的负面影响以及对人类尤其是儿童健康的潜在不利影响，已列入REACH法规的SVHC清单。现有PVC密封条缺点主要为：表面发粘，手感差，回弹性不好，耐寒性差，不耐迁移，溶剂抽出性能较差，容易腐蚀冰箱内胆与侧板等问题。为提高PVC密封条产品的回弹性，有采用丁腈、CR、EVA等弹性体对PVC材料进行改性。中国专利CN103073828A公开了...
【技术保护点】
一种PVC的组合物，该组合物包含以下组分：100重量份的PVC树脂；30～1500重量份的TPU，优选40～1200重量份，更优选50～900重量份。
【技术特征摘要】
1.一种PVC的组合物，该组合物包含以下组分：100重量份的PVC树脂；30～1500重量份的TPU，优选40～1200重量份，更优选50～900重量份。2.根据权利要求1所述的PVC组合物，其特征在于，所述TPU的硬度不高于90A，优选不高于85A，更优选不高于80A；TPU的流动温度不高于180℃，优选不高于170℃，更优选不高于160℃。3.根据权利要求1所述的PVC组合物，其特征在于，所述PVC树脂的平均聚合度为650～2500，优选为750～1700，更优选为800～1300。4.根据权利要求1-3中任一项所述的PVC/组合物，其特征在于，所述组合物还包含添加0.05～20重量份的手感改性剂，优选0.1～18重量份，更优选0.3～16重量份；所述的手感改性剂为球形有机硅颗粒，粒径为1～100um，优选2～80um，更优选5～70um。5.根据权利要求1-4中任一项所述的PVC组合物，其特征在于，任选地添加0～150重量份增塑剂，优选2～130重量份，更优选5～110重量份；所述增塑剂为选自苯多羧酸酯、聚酯增塑剂、脂肪族二元羧酸酯、环氧增塑剂、对苯二甲酸酯、柠檬酸酯和多元醇酯中的一种或多种；任选地添加0～120重量份填料，优选2～110重量份，更优选5～100重量份；所述填料为碳酸钙、滑石...
【专利技术属性】
技术研发人员：潘勇军，李万庆，杨万庆，高玉宝，黄岐善，
申请(专利权)人：万华化学集团股份有限公司，
类型：发明
国别省市：山东,37