The invention relates to a method for finishing crease resistant finishing of pure cotton fabric by using biological polishing waste liquid, which belongs to the field of textile printing and dyeing technology. The invention adopts the following process: (1) the conventional cellulase bio polishing processing waste water filtration, and then concentrated, to reach 2 cellulase protein 4g/L concentration in the water; (2) adding dosage of polycarboxylic acids and fully dissolved, the solution temperature reaches 95 degrees Celsius, 60 heat treatment 80min; (3) adding conventional catalyst and stirring fully dissolved, will be processed cotton fabrics in conventional curing process on the fabric wrinkle treatment. The method uses the polishing waste liquid to prepare the polycarboxylic acid finishing liquid to crease the cotton fabric, realizes the recycling of the waste liquid, and strengthens the anti crease effect of the polycarboxylic acid on the cotton fabric by using the residual cellulase.
【技术实现步骤摘要】
一种利用生物抛光废液对棉织物进行防皱整理的方法
本专利技术涉及一种利用生物抛光废液对纯棉织物进行防皱整理的方法，属于纺织印染
技术介绍
棉纤维织物具有很多优良特性，但在穿着过程中易起皱且皱痕不易消除，不像毛织物、合成纤维织物那样在服用过程中能保持平整的外观，于是便出现了以提高织物弹性和增强棉织物从折皱中回复原状能力为主要目的的防皱整理。早期的防皱整理剂存在甲醛释放的问题，其应用受到限制。因此，对棉织物无甲醛防皱整理剂的开发研究日趋活跃，主要包括双羟乙基砜类化合物、环氧类化合物、反应型聚氨酯、反应性有机硅类化合物、天然高分子化合物和多元羧酸类化合物等。综合考虑整理后织物的多方面性能，许多研究者认为多元羧酸类化合物最有可能取代传统的防皱整理剂，其中以1,2,3,4-丁烷四羧酸（BTCA）和柠檬酸的应用最为广泛。各类助剂如聚乙二醇、三乙醇胺、壳聚糖、纳米氧化物、柔软剂等被添加入整理浴中对多元羧酸防皱起辅助作用，效果也不尽相同。
技术实现思路
本专利技术的目的是利用棉织物生物抛光废液配制多元羧酸防皱整理液，实现废液回收利用，并借助残留的纤维素酶增强多元羧酸对棉织物的...
【技术保护点】
一种利用生物抛光废液对纯棉织物进行防皱整理的方法，其特征在于采用以下工艺：（1）将常规的纤维素酶生物抛光废液过滤，然后进行浓缩，使纤维素酶蛋白在水中的浓度达到2‑4g/L;（2）加入常规用量的多元羧酸整理剂并充分溶解，将处理液温度升至95℃，保温处理60‑80min；（3）加入常规用量催化剂并充分搅拌溶解，将待处理棉织物浸入，采用常规焙烘工艺对织物进行防皱处理。
【技术特征摘要】
1.一种利用生物抛光废液对纯棉织物进行防皱整理的方法，其特征在于采用以下工艺：（1）将常规的纤维素酶生物抛光废液过滤，然后进行浓缩，使纤维素酶蛋白在水中的浓度达到2-4g/L;（2）加入常规用量的多元羧酸整理剂并充分溶解，将处理液温度升至95℃，保温处理60-80min；（3）加入常规用量催化剂并充分搅拌溶解，...
【专利技术属性】
技术研发人员：郝龙云，王蕊，蔡玉青，房宽峻，
申请(专利权)人：青岛大学，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。