一种金属铜缓蚀剂制造技术

本发明专利技术公开了一种金属铜缓蚀剂，为植酸(PA)微胶囊包覆的3‑硫基‑4‑甲基‑1,2,4‑三氮唑(4‑MTTL)，即PA@4‑MTTL微胶囊；4‑MTTL分子占据PA@4‑MTTL微胶囊之间的孔隙；还公开了该金属铜缓蚀剂的制备方法及其在抑制金属铜腐蚀中的应用。该金属铜缓蚀剂由于4‑MTTL分子能够占据PA@4‑MTTL微胶囊之间的空隙而具有高缓蚀性能，4‑MTTL分子从PA@4‑MTTL微胶囊释放，起到自修复物理划痕的功能。

A corrosion inhibitor for copper metal

The invention discloses a metal copper corrosion inhibitor, phytic acid (PA) 3 Sbased microcapsules containing 4 methyl 1,2,4 three triazole (4 MTTL), namely PA@4 MTTL microcapsule; 4 MTTL PA@4 MTTL molecules occupy the pore spaces between the microcapsules also disclosed; the preparation method of the copper corrosion inhibitor and its application in the inhibition of copper corrosion in metal. The metal corrosion inhibitor of copper for 4 MTTL molecules can occupy the PA@4 gap between the MTTL microcapsule has high corrosion inhibition performance of 4 MTTL molecules from the PA@4 MTTL microcapsules release to the physical function of self repairing scratches.

【技术实现步骤摘要】
一种金属铜缓蚀剂
本专利技术涉及金属材料的防腐蚀
，尤其涉及一种金属铜缓蚀剂。
技术介绍
材料的腐蚀，尤其是金属，会导致大量的生命财产损失以及环境污染。例如铜及其合金，因具有高导热导电性和良好的韧性、机械加工性以及相对低廉的价格，被广泛应用于多个领域，包括建筑、电缆电线、电子设备、生物医学、工业工厂等等。然而，铜金属在潮湿的空气或液体中，尤其是在酸性环境中或存在氯离子的情况下很容易被腐蚀。由于这种腐蚀行为，每年都会发生严重的经济作物损失、能源浪费及人员伤亡。以管道系统为例，海水中不受控制的腐蚀可能会导致泄漏和爆炸，其之后会影响整个海洋环境和生态系统。因此，人们进行了各方面的努力以限制这种影响，例如表面涂层、可控制渗透性模板、阴极和阳极保护等等。其中，在铜表面上使用缓蚀剂获得了很大的关注。抗腐蚀的涂层种类繁多，大致上可以分为金属涂层、无机涂层和有机涂层。然而，尽管抑制剂涂层可以保护金属免受腐蚀，有许多原因可能导致涂层失败，例如有瑕疵的涂层或机械性能的改变。经历这种导致裂纹或点蚀的涂层改变，金属更可能会暴露于恶劣的腐蚀环境，如3wt.％NaCl溶液，其随后会蔓延并将基底暴露于大气水本文档来自技高网...

【技术保护点】
一种金属铜缓蚀剂，其特征在于，所述金属铜缓蚀剂为植酸微胶囊包覆的3‑硫基‑4‑甲基‑1,2,4‑三氮唑，即PA@4‑MTTL微胶囊。

【技术特征摘要】
1.一种金属铜缓蚀剂，其特征在于，所述金属铜缓蚀剂为植酸微胶囊包覆的3-硫基-4-甲基-1,2,4-三氮唑，即PA@4-MTTL微胶囊。2.根据权利要求1所述的金属铜缓蚀剂，其特征在于，3-硫基-4-甲基-1,2,4-三氮唑分子占据所述PA@4-MTTL微胶囊之间的孔隙。3.根据权利要求1所述的金属铜缓蚀剂，其特征在于，所述植酸微胶...