一种防止涂机钝化药液料盘溢液的方法技术
Method for preventing coating machine from passivating liquid plate overflow
The invention relates to the field of zinc plating passivation treatment, in particular to a method for preventing the coating machine from passivating the overflow of the liquid medicine plate. The process of this method are as follows: feeding pump, liquid overflow pipe, plate passivation, passivation liquid recovery tank, liquid tank height reduce passivation, passivation liquid tank to the passivation coating machine equipment is passivating liquor tank tray and passivation liquid level difference exists, then the passivation liquid tray level high, higher than the liquid overflow through the overflow pipe recovery. The invention improves the circulation mode of the passivation liquid medicine, avoids the abnormal waste caused by the passivation liquid plate overflow, improves the quality of the passivation product and reduces the passivation spot defect.
【技术实现步骤摘要】
一种防止涂机钝化药液料盘溢液的方法
本专利技术涉及镀锌钝化处理领域，具体为一种防止涂机钝化药液料盘溢液的方法。
技术介绍
镀锌是目前采用最为广泛的钢铁防腐手段，但是由于锌层在空气中，尤其是潮湿环境中容易被腐蚀，所以还要对镀锌后的钢板进行后处理工艺进一步提高产品防腐性能，热镀锌板常见的后处理方式主要有钝化处理、磷化处理、耐指纹处理以及涂油处理，钝化是用铬酸盐溶液与金属作用，在其表面生成三价或六价铬化层。这层膜通常是氧化剂和基体金属的化合物。能够抑制锌层的阳极反应.从而保护了锌层。目前广泛使用的钝化处理方式主要分为：浸泡式、喷淋式及辊涂式三种，连续镀锌机组采用的是辊涂式处理方法，钝化药液由工作罐打入料盘中，通过一个提料辊将钝化药液送到涂辊，涂辊再以一定的压力和速度将钝化药液涂在带钢表面。如图2所示，镀锌机组原有的设计中，涂机料盘供料方式如下：进料泵→钝化药液料盘→回料泵→钝化药液槽，钝化药液料盘位于提料辊下部，钝化药液槽位于涂机侧部。当出现回料泵故障时，只由进料泵向钝化药液料盘内打药工作，多余药液无法回收造成钝化药液料盘内部液位升高溢出。如图1所示，现有方法使带钢表面...
【技术保护点】
一种防止涂机钝化药液料盘溢液的方法，其特征在于，该方法的流程如下：进料泵→钝化药液料盘→溢流管回收→钝化药液槽，降低钝化药液槽高度，钝化药液槽移至涂机钝化设备下部，使钝化药液槽与钝化药液料盘存在液位差后，再将钝化药液料盘液位限高，高于此液位后溢流通过溢流管回收。
【技术特征摘要】
1.一种防止涂机钝化药液料盘溢液的方法，其特征在于，该方法的流程如下：进料泵→钝化药液料盘→溢流管回收→钝化药液槽，降低钝化药液槽高度，钝化药液槽移至涂机钝化设备下部，使钝化药液槽与钝化药液料盘存在液位差后，再将钝化药液料盘液位限高，高于此液位后溢流通过溢流管回收。2.按照权利要求1所述的防止涂机钝化药液料盘溢液的方法，...
【专利技术属性】
技术研发人员：张扬，刘晓峰，赵兴时，刘万中，崔成慧，张玉辉，
申请(专利权)人：本钢板材股份有限公司，本钢浦项冷轧薄板有限责任公司，
类型：发明
国别省市：辽宁,21