The invention relates to a microwave absorbing material, including absorbing agent, expandable microspheres and resin, the suction mass percentage of wave agent is 30% ~ 80%; the mass percentage of expandable microspheres was 1% ~ 3%; the mass percentage of the resin was 30% ~ 40%. The absorbing material provided by the invention using expandable microsphere foaming prepared in the preparation process of absorbing wave material in the foam expansion ball is basically the same, foam density is basically the same, the absorbing material can obtain better absorbing properties. In addition, the preparation method of the wave absorbing material has relatively low requirements for the equipment, and the production technology is less difficult.
【技术实现步骤摘要】
吸波材料及其制备方法
本专利技术涉及吸波材料，更具体地涉及吸波材料及其制备方法。
技术介绍
随着科学技术发展的日新月异，以电磁波为媒介的各种技术和产品越来越多，电磁波辐射对环境的影响也日益增大。比如，无线电波可能对机场环境造成干扰，导致飞机航班无法正常起飞；移动电话可能会干扰各种精密电子医疗器械的工作；即使是普通的计算机，也会发射携带信息的电磁波，它可能在几公里以外被接收和重视，造成国防、政治、经济、科技等方面情报的泄露。因此，治理电磁污染，寻找一种能抵挡并削弱电磁波辐射的材料——吸波材料，已成为材料科学的一大课题。吸波材料是能吸收投射到它表面的电磁波能量的一类材料，其在包括军事以及其它方面也有广泛的应用，比如隐形机、隐形衣等。材料吸收电磁波的基本条件是：(1)电磁波入射到材料上时，它能最大限度地进入材料内部，即要求材料具有匹配特性；(2)进入材料内部的电磁波能迅速地几乎全部衰减掉，即衰减特性。波吸收材料按照损耗机理，可分为介电型吸波材料和磁介质型吸波材料，主要包括铁氧体、金属微粉、钛酸钡、碳化硅、石墨、导电纤维、纳米材料、导电聚合物等。而按照吸波材料的成型工艺，...
【技术保护点】
一种吸波材料，其特征在于，包括吸波剂、可膨胀微球和树脂，所述吸波剂的质量百分比为30％～80％；所述可膨胀微球的质量百分比为1％～3％；所述树脂的质量百分比为30％～40％。
【技术特征摘要】
1.一种吸波材料，其特征在于，包括吸波剂、可膨胀微球和树脂，所述吸波剂的质量百分比为30％～80％；所述可膨胀微球的质量百分比为1％～3％；所述树脂的质量百分比为30％～40％。2.根据权利要求1所述的吸波材料，其特征在于，所述吸波剂为铁氧体、金属微粉、钛酸钡、碳化硅、石墨、导电纤维、纳米材料或导电聚合物等吸波剂中的至少一种。3.根据权利要求1所述的吸波材料，其特征在于，所述可膨胀微球为热胀性的球状塑料颗粒。4.根据权利要求3所述的吸波材料，其特征在于，所述可膨胀微球起始直径为5-20μm，受热膨胀后直径为20-150μm。5.根据权利要求1所述的吸波材料，其特征在于，所述树脂为环氧树脂、丙烯酸树脂、酚醛树脂或双马树脂等热固性树脂中的至少一种。6.一种权利要求1～5中任一项所述的吸波材料的制备方法，其特征在于，包括以下步骤：将吸波剂、可膨胀...
【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：深圳光启高等理工研究院，深圳光启创新技术有限公司，
类型：发明
国别省市：广东,44