The invention discloses a white foxing glue is not easy to burn, which is characterized in that, according to the weight calculation, including: 70 90, standard rubber polybutadience rubber 10 30, 1.3 1.5, ultramarine 6 4 zinc oxide, stearic acid, silica 15 3 1 25, titanium dioxide 40 50, M 0.4 accelerator 0.6, accelerator DM 1.6 1.8, 0.1 0.2, accelerator D C 1 antioxidant SP 3, 1.6 2.0, sulfur 8, RX 4 industrial grease 80 resin 6 8, calcium carbonate 80, 0.3 0.5, antiscorching salicylic acid agent CTP 0.1 0.5. The invention has the advantages that the compound composition with salicylic acid and antiscorching agent CTP used to prevent scorch phenomenon, using this formula to produce foxing glue not prone to scorch phenomenon, safety rubber processing greatly improved. At the same time antiscorching agent CTP has been exposed to high heat or light rubber scorch has restoration function, can further improve the processing safety, avoid increasing air temperature, and temperature caused by excessive scorch loss.
【技术实现步骤摘要】
一种不易焦烧的白色围条胶
本专利技术涉及橡胶材料制备领域，涉及鞋用边胶配方，尤其涉及一种不易焦烧的白色围条胶。
技术介绍
焦烧是一种胶料早期硫化现象，产生焦烧的原因有：配合不当，如硫化剂、促进剂用量太多；操作不当，如辊温过高、过早加入硫黄、或加入硫化剂后混炼时间太长。混炼不均造成硫化剂和促进剂局部集中；胶料冷却停放不当。如停放过久，停放场地温度过高或空气流通等，出现焦烧现象时，胶料表面不光滑，麻面可塑度降低，严重时胶料表面会出现大小不等的颗粒。由于夏季气温较高，容易造成运动鞋用白色围条胶在混炼机加工时发生焦烧现象，造成胶料报废。
技术实现思路
本专利技术的目的是针对现有技术的不足，而提供一种不易焦烧的白色围条胶，用该配方生产的围条胶不易发生焦烧现象，能大幅提高胶料加工的安全性。实现本专利技术目的的技术方案是：一种不易焦烧的白色围条胶，按照重量份计算，包括：标准橡胶70-90、顺丁胶10-30、群青1.3-1.5、氧化锌4-6，硬脂酸1-3、白炭黑15-25、钛白粉40-50、促进剂M0.4-0.6、促进剂DM1.6-1.8、促进剂D0.1-0.2、防老剂SP-C1-3...
【技术保护点】
一种不易焦烧的白色围条胶，其特征在于，按照重量份计算，包括：标准橡胶70‑90、顺丁胶10‑30、群青1.3‑1.5、氧化锌4‑6，硬脂酸1‑3、白炭黑15‑25、钛白粉40‑50、促进剂M 0.4‑0.6、促进剂DM 1.6‑1.8、促进剂D 0.1‑0.2、防老剂SP‑C 1‑3、硫磺1.6‑2.0、工业脂4‑8、RX‑80树脂 6‑8、碳酸钙 80、水杨酸0.3‑0.5、防焦剂CTP 0.1‑0.5。
【技术特征摘要】
1.一种不易焦烧的白色围条胶，其特征在于，按照重量份计算，包括：标准橡胶70-90、顺丁胶10-30、群青1.3-1.5、氧化锌4-6，硬脂酸1-3、白炭黑15-25、钛白粉40-50、促进剂M0.4-0.6、促进剂DM1.6-1.8、促进剂D0.1-0.2、防老剂SP-C1-3、硫磺1.6-2.0、工业脂4-8、RX-80树脂6-8、碳酸钙80、水杨酸0.3-...